사출금형의 5축 고속가공에서 공구자세에 따른 가공 특성에 관한 연구
강익수(I. S. Kang),김석원(S. W. Kim),김정석(J. S. Kim),이기용(K. Y. Lee) 한국생산제조학회 2006 한국공작기계학회 춘계학술대회논문집 Vol.2006 No.-
The high speed machining has been widely applied to manufacture a die and machine elements product in industrial field. Especially, 5-axis milling has been employed to produce a wide range of turbine blades, impellers and complex molds. In this study, machining characteristics of injection mold was investigated according to tool position control. The cutting force and surface roughness were measured with various tool position angles. When the tool position angle was over 25 degree, the cutting force was decreased and surface roughness was good compared with low tool position angles.
비정질 As₂S₃를 중간층으로 하는 Fabry - Perot 에탈론에서의 광쌍안정에 관한 연구
김강호(K. H. Kim),김석원(S. W. Kim),한성홍(S. H. Hahn) 한국광학회 1997 한국광학회지 Vol.8 No.6
광학 다층박막 증착법으로 비정질 As₂S₃를 중간층으로 하고 앞뒷면 거울의 반사율을 다르게 한 비대칭 Fabry-Perot 에탈론을 구성하고 광의 편광에 따른 광쌍안정 현상을 관찰하였다. 사용된 중간층의 광학적 두께는 광원인 Ar+(λ=514.5 ㎚) 레이저 광에 대하여 2λ가 되도록 하였다. Ar+ 레이저의 출력이 80~100 ㎽ 일 때 광쌍안정 현상이 관측되었고, 입사되는 광의 각 편광상태에 따라 반사와 투과하는 광의 경향이 서로 다름을 알 수 있었으며, 이는 광의 편광에 따른 비대칭 Fabry-Perot 에탈론내에서의 위상차가 입사광의 세기에 따라 다르기 때문인 것으로 해석되어 질 수 있다. We fabricated the asymmetric Fabry-Perot etalon which contains amorphous As₂S₃ as a spacer layer by using the method of optical multilayer coating and observed the optical bistability with the polarization. Optical thickness of the spacer layer is 2λ at Ar+ (λ=514.5 ㎚) laser wavelength. Optical bistability was observed at the intensities between 80~100 ㎽ and the experiment shows us that the trends of bistable loop of the reflected and the transmitted lights are quite different depending on the state of polarization. This phenomena can be explained as the phase differences of each polarizations are different in the nonlinear Fabry-Perot etalon.
자동차 부품용 내열, 고온 내산화성 고Si 구상흑연주철의 제조기술개발
김석원(S. W. Kim),우기도(K. D. Woo),한상원(S. W. Han),김정규(J. K. Kim) 한국자동차공학회 1996 한국자동차공학회 춘 추계 학술대회 논문집 Vol.1996 No.6_1
The study aims to compare the characteristics of high temperature oxidation in various High Si Ductile Cast Iron (HSOCI) in order to improve the material for exhaust manifolds which require stronger heat resistance. The specimens containing 2~6% Si and 0~4%Mo were heated in 650℃~950℃ for 100hrs, and 650℃ for 5~20 day. Consequently, amount of oxidation were decreased<br/> with increase of Si, Mo, due to the formation of Fe₂SiO₄and Mo carbide. As the amount of Si and Mo increase, hardness is increased but charpy impact energy in deceased. This is because that the Si solution and Mo carbide in matrix increase with increase of Si, Mo. As a result of addition of various alloy elements in the cast iron which contained 3.5%C, anti-oxidation property is improved, but toughness is decreased with increase of Si, Mo