알콕사이드로부터 Mullite 분말의 합성 및 Mullite-Zirconia 복합체의 특성
함종근,이홍림 한국세라믹학회 1990 한국세라믹학회지 Vol.27 No.2
The mullite-15v/o ZrO2 composites were prepared by dispersing ZrO2-3m/o Y2O3 powders into the mullite matrix in order to improve the mechanical properties of the mullite. The densification and retention of t-ZrO2 in the matrix of synthetic mullite were also investigated. From IR spectroscopic analysis, the obtained amorphous SiO2-Al2O3 powder was observed to have Si-O-Al chemical bond in its structure which might result in the homogeneous mullite composition. The lattice parameter of the mullite powder calcined above 130$0^{\circ}C$ (a0=7.5468$\AA$) is nearly close to the value of stoichiometric mullite (71.8wt% Al2O3, a0=7.5456$\AA$). The sintering behavior, microstructure, flexural strength and fracture toughness of the mullite and mullite-15v/o ZrO2 composites have been studied. The mullite-15v/o ZrO2(+3m/o Y2O3) ceramics with relative densities of 96% were obtained when sintered at 1$600^{\circ}C$. The flexural strength and fractrue toughness of the composites sintered at 1$600^{\circ}C$(calcination temperature of mullite powders ; 125$0^{\circ}C$) had maximum values of 307MPa and 2.50MPa.m1/2, respectively. The fracture toughness improvement in the mullite-ZrO2 cmoposite is assumed to be resulted from the combined effect of the stress-induced phase transformation of tetragonal ZrO2 and the crack deflection due to microcracking by the monoclinic ZrO2 formation.
-
이홍림,함종근 한국세라믹학회 1989 한국세라믹학회지 Vol.26 No.6
A very fine and pure mullite powder of the stoichiometric composition was prepared from aluminium isopropoxide and tetraethylorthosilicate by an alkoxide hydrolysis method using NH4OH as a catalytic agent. The gel powder obtained from the hydrolysis was calcined at 80$0^{\circ}C$ and 125$0^{\circ}C$. The average particle sizes of the powders calcined at 80$0^{\circ}C$ and 125$0^{\circ}C$ were 0.19${\mu}{\textrm}{m}$ and 0.25${\mu}{\textrm}{m}$, respectively. The specific surface areas of the powders calcined at 80$0^{\circ}C$ and 125$0^{\circ}C$ were 114.7$m^2$/g and 20.6$m^2$/g, respectively. The bending strength and fracture toughness of the mullite ceramics sintered at 1$650^{\circ}C$ were 263.1MPa and 2.30MPa.m1/2 respectively.