석탄폐석을 이용한 소다라임계 컬러유리의 광학적 특성

임태영,정상수,황종희,김진호,김정국,Lim, Tae-Young,Jeong, Sang-Su,Hwang, Jong-Hee,Kim, Jin-Ho,Kim, Jung-Kook 한국재료학회 2010 한국재료학회지 Vol.20 No.10

Glass was fabricated using refused coal ore obtained from the Dogye coal mine in Samcheok. We additionally used soda ash and calcium carbonate to make a glass with the chemical composition of soda-lime glass, and we also used white, brown, and green glass cullet to make various kinds of colored glass. Transparent glass was fabricated by melting batch materials including refused coal ore at $1550^{\circ}C$ for 1 hr in an electrical furnace. The light transmittance and color chromaticity were measured by a UV/VIS/NIR spectrometer. Transparent glass with a light transmittance of over 80% was fabricated using normal refused coal ore and white glass cullet. Various kinds of colored glass with a light transmittance of 30-80% were fabricated using refused coal ore and brown or green glass cullet. The light transmittance of the mixed color glass samples, fabricated using normal refused coal ore and brown glass cullet and green glass cullet, indicated 30-47%, a relatively low value, in the condition of a cullet ratio of 20-50%. The characteristics of the color chromaticity of the glass samples were indicated in a chromaticity diagram by x-coordinates, y-coordinates, Y (lightness). The values of x-coordinates and y-coordinates were moved with a regular directional property according to the kind and amount of glass cullet. Therefore, we concluded that refused coal ore can be used for raw materials of color glass products like art glass and glass tile.

석탄 폐석을 이용한 소다라임계 유리의 제조 및 특성 연구

임태영,정상수,황종희,김진호,Lim, Tae-Young,Jeong, Sang-Su,Hwang, Jong-Hee,Kim, Jin-Ho 한국결정성장학회 2010 한국결정성장학회지 Vol.20 No.1

삼척 도계지역의 탄광에서 석탄채취시에 발생되는 석탄폐석을 이용하여 유리를 제조하였다. 소다라임계 화학조성을 갖는 유리를 제조하기 위하여 화학원료로서 소다회, 탄산칼슘 등의 원료를 추가로 사용하였고, 화학원료인 탄산칼슘 대신에 천연광물원료인 석회석을 사용하였을 때의 특성을 검토하였다. 전기로를 사용하여 $1,550^{\circ}C$에서 1시간 용응하여 투명한 유리를 제조할 수 있었다. 석탄폐석의 종류 및 파유리의 종류에 따라 다양한 종류의 유리샘플이 제조되었다. 유리샘플의 투과율 및 색차와 같은 광학적 특성을 UV/VIS/NIR Spectrometer를 이용하여 측정하였고, 또한 열팽창계수 및 연화점과 같은 열적특성도 측정하였다. 그 결과, 일반 선탄경석으로는 70% 이상의 가시광선투과율을 갖는 투명한 유리를 제조할 수 있었으며, 또한 쉘(shell) 타입의 선탄경석으로는 0~35%의 가시광선 투과율을 갖는 검정색의 칼라유리를 제조할 수 있었다. 따라서 석탄폐석을 이용하여 건축재료로서 유리타일이나 발포유리와 같은 유리 2차제품을 제조하는데 활용할 수 있으리라 판단되었다. Glass was fabricated by using refused coal ore obtained from Dogye coal mine in Samchuk. We additionally used soda ash and calcium carbonate as raw materials to make a glass with the chemical composition of soda-lime glass. And the properties of glass were measured when limestone was used as natural raw materials instead of calcium carbonate as chemical raw materials. Transparent glass was fabricated by melting raw materials at $1550^{\circ}C$ for 1 hr in an electrical furnace. The various kinds of glass samples were fabricated according to the kinds of refused coal ore and glass cullet. The optical properties of transmittance and color chromaticity were measured by UV/VIS/NIR spectrometer and the thermal properties of thermal expansion coefficient and softening point were measured. Transparent glass with the transmittance of over 70% in visible range was fabricated by using normal refused coal ore and black colored glass with the transmittance of 0~35% was fabricated by using shel1 type refused coal ore. Therefore, it is concluded that refused coal ore can be used for raw materials to manufacture secondary glass products such as a glass tile and foamed glass panel for construction material.

다공성 세라믹 소재를 이용한 분자인식기술 개발

임태영,김진호 한국세라믹학회 2009 세라미스트 Vol.12 No.6

자동착자 및 검사자동화 시스템을 위한 집적회로 설계

임태영,이천희,Im, Tae-Yeong,Lee, Cheon-Hui 한국정보처리학회 1999 정보처리논문지 Vol.6 No.7

본 논문은 TV 브라운관과 컴퓨터 모니터에 사용되는 마그네트(Magnet)에 일정한 자력을 갖도록 자화 시키는 착자기를 제어하며, 검사공정을 자동화하는 제어 시스템용의 집적회로를 설계하여 개발한 것에 관한 것으로써, 착자기의 콘트롤 모듈과 프로토콜 모듈의 주변기기 제어회로 부분을 0.8um CMOS SOG 기술로 설계하여 ETRI에서 공정하여 칩(Chip)을 완성시켜 동작을 확인하였다. 본 논문에서는 개별 셀(Single cell)의 지연 예측에 사용되었던 기존의 프로파게이션/램프 지연 모델(Propagation/ramp delay model)을 분석, 문제점을 보완 수정한 LODECAP(LOgic DEsign CAPture)의 인버터 선형 지연 모델을 응용하여 타이밍 콘트롤 블록 내의 지연 체인(Delay chain)을 설계 할 수 있는 새로운 "지연 예측 수식"을 제안하였다. 본 논문은 추출된 수식에 의거하여 타이밍 콘트롤 블록의 설계, 시스템에 적용하였으며, 나머지 블록들을 설계한 기법에 대하여도 상술하였다.여도 상술하였다. In this paper a VLSI design for the automatic magnetizing and inspection system has been presented. This is a design of a peripheral controller, which magnetizes CRTs and computer monitors and controls the automatic inspection system. We implemented a programmable peripheral interface(PPI) circuit of the control and protocol module for the magnetizer controller by using a 0.8um CMOS SOG technology of ETRI. Most of the PPI functions have been confirmed. In the conventional method, the propagation/ramp delay model was used to predict the delay of cells, but used to model on only a single cell. Later, a modified "linear delay predict model" was suggested in the LODECAP(LOgic DEsign CAPture) by adding some factors to the prior model. But this has not a full model on the delay chain. In this paper a new " delay predict equation" for the design of the timing control block in PPI system has been suggested. We have described the detail method on a design of delay chain block according to the extracted equation and applied this method to the timing control block design. And we had descriptions on the other blocks of this system.

Sol-gel 법에 의해 $SnO_2$계 박막위에 코팅된 $TiO_2$ 박막의 특성

임태영,조혜미,김진호,황종희,황혜진,Lim, Tae-Young,Cho, Hye-Mi,Kim, Jin-Ho,Hwang, Jong-Hee,Hwang, Hae-Jin 한국결정성장학회 2009 한국결정성장학회지 Vol.19 No.5

Sol-gel법에 의해 친수성 투명 $TiO_2$ 박막이 제조되었고, 박막의 접촉각, 표면구조, 투과율의 특성이 측정되었다. 더욱이 박막의 친수 특성을 향상시키기 위하여 계면활성제 tween 80이 이용되었다. Tween 80의 첨가량이 0, 10, 30, 50wt%일 때, 제조된 박막의 접촉각은 각각 $41.4^{\circ}$, $18.2^{\circ}$, $16.0^{\circ}$, $13.2^{\circ}$로 확인되었다. 제조된 $TiO_2$ 박막은 자외선 조사 후 Methylene blue용액을 분해시켜 흡광도를 감소시키는 광촉매 특성을 보여주었다. 일반유리(bare glass), Antimony Tin Oxide(ATO)코팅 유리, Fluorine Tin Oxide(FTO)코팅유리, Indium Tin Oxide(ITO)코팅유리 기판 위 에 Tween 80을 30 wt% 함유한 $TiO_2$ 용액을 적층하여 박막의 접촉각과 투과율을 측정하였다. 다양한 기판에 제조된 박막은 $16.2\sim27.1^{\circ}$의 표면 접촉각을 나타냈으며 자외선 조사 후에는 접촉각이 $13.2\sim17.6^{\circ}$로 낮아졌다. 특히 ATO코팅유리와 FTO 코팅유리 기판 위에 코팅된 필름은 가시광선 영역에서 각각 74.6%, 76.8%의 높은 투과율을 나타내었고, 적외선 영역에서는 각각 54.2%, 40.4%의 낮은 투과율을 나타냈다. Hydrophilic and transparent $TiO_2$ thin film was fabricated by sol-gel method and the properties of contact angle, surface morphology, and transmittance were measured. In addition, surfactant Tween 80 was used for increasing the hydrophilic property of thin film. When the contents of Tween 80 in $TiO_2$ solution was 0, 10, 30, 50wt%, the contact angles of $TiO_2$ thin film were $41.4^{\circ}$, $18.2^{\circ}$, $16.0^{\circ}$, $13.2^{\circ}$, respectively. Fabricated $TiO_2$ thin film showed the photocatalytic property that decomposed methylene blue and decreased the absorbance of solution after UV irradiation. $TiO_2$ thin films fabricated with the solution of 30 wt% Tween 80 were deposited on glass (bare), antimony tin oxide (ATO), fluorine tin oxide (FTO), indium tin oxide (ITO) coated glass substrates, and the contact angle and transmittance of thin film was measured. The contact angles of thin films deposited on four substrates were $16.2\sim27.1^{\circ}$ and was decreased to the range of $13.2\sim17.6^{\circ}$ after UV irradiation, Especially, the thin films coated on ATO and FTO glass substrate showed high transmittance of 74.6% in visible range, respectively, and low transmittance of 54.2% and 40.4% in infrared range, respectively.

인터럽트 발생기를 사용한 접속 비트 전환식 양방향 접속장치의 설계

임태영,이천희,Lim, Tae-Young,Yi, Cheon-Hee 대한전자공학회 1999 電子工學會論文誌, C Vol.c36 No.7

본 논문에서는 접속된 주변장치와 데이터를 비동기로 교환 할 수 있는 접속 비트 전환식 양방향 접속 장치 설계에 대하여 기술한다. 특히 인터럽트 발생기를 설계하기 위해서 제시된 펄스형 순차회로 파형을 합성할 수 있는 진리치 비교 알고리즘을 제안하고 이를 인터럽트 레지스터 설계에 적용한 것에 대하여 상술하였다. 또한 개별 비트 출력 신호들의 클럭 스큐 현상을 없애기 위한 최종 출력 핀 제어 기법을 시스템에 적용하였으며 나머지 블록들을 설계한 기법에 대하여도 상술하였다. 이러한 기법을 사용함으로써 본 논문의 접속 포트들은 0.7ns 이내의 지연시간을 나타내었다. In this paper, Bit selectable and Bi-directional Interface Device is described, which can communicate data with the peripheral devices. Specially, an algorithm of truth-table comparison that synthesizes the pulse-type sequential circuit pulse has been proposed to design the Interrupt Generator, and implemented in designing the Interrupt Register. Also, a description of the asynchronous design method is given to remove the clock skew phenomenon, and the output asynchronous control method which finds the optimal clock and controls all the enable signal of the output pins at the same time is presented. Using this technique interface ports have delay time of less-than 0.7ns.

솔-젤 Dip Coating에 의한 Sb-doped $SnO_2$ 투명전도막의 제조 및 특성

임태영,오근호 한국결정성장학회 2003 韓國結晶成長學會誌 Vol.13 No.5

ATO(antimony-doped tin oxide) 투명전도막을 sol-gel dip coating 방법에 의해 $SiO_2$/glass 기판 위에 성공적으로 제조하였다 ATO막의 결정상은 $SnO_2$상임을 확인하였고, 막의 두께는 withdrawal speed를 50 mm/minute로 코팅시 약 100 nm/layer였다. $SiO_2$/glass 기판 위에 코팅한 400 nm두께의 ATO 박막을 질소분위기에서 annealing한 후, 측정한 광 투과율과 전기 저항치는 각각 84%와 $5.0\times 10^{-3}\Omega \textrm{cm}$였다. 이러한 특성은 $SiO_2$막이 Na 이온의 확산을 제어하여 $Na_2SnO_3$ 및 SnO와 같은 불순물의 형성을 억제하고, 막 내부의 Sb의 농도와 $Sb^{3+}$에 대한 $Sb^{5+}$의 비를 증가시키는데 기여했기 때문으로 확인되었다. 또한, $N_2$ annealing은 $Sb^{5+}$뿐만 아니라 $Sn^{4+}$를 환원시킴으로써 전기전도도를 향상시킴을 확인하였다. The transparent conducting thin film of ATO (antimony-doped tin oxide) was successfully fabricated on$SiO_2$/glass substrate by a sol-gel dip coating method. The crystalline phase of the ATO thin film was identified as SnO$_2$ major phase and the film thickness was about 100 nm/layer at the withdrawal speed of 50 mm/minute. Optical transmittance and electrical resistivity of the 400 nm-thick ATO thin film which was annealed under nitrogen atmosphere were 84% and $5.0\times 10^{-3}\Omega \textrm{cm}$, respectively. It was found that the $SiO_2$ layer inhibited Na ion diffusion and the formation of impurities like $Na_2SnO_3$ or SnO while increasing Sb ion concentration and higher ratio of $Sb^{5+}/Sb^{3+}$in the film. Annealing at nitrogen atmosphere leads to the reduction of $Sn^{4+}$ as well as $Sb^{5+}$ resulting in decrease of the electrical resistivity of the film.

비대상성 간경변을 동반한 진행성 간세포성 간세포암에서 저용랑 5-FU 및 Cisplatin 주입요법에 의한 생존율 향상

임태영,정재연,조성원,심성준,최준혁,최혜진,이기명,김재근,원제환,유병무,이광재,함기백,김진홍 대한내과학회 2004 대한내과학회 추계학술대회 Vol.2004 No.1

석탄 폐석을 이용한 발포유리의 제조 및 물리적 특성 연구

임태영,구현우,황종희,김진호,김정국,Lim, Tae-Young,Ku, Hyun-Woo,Hwang, Jong-Hee,Kim, Jin-Ho,Kim, Jung-Kook 한국결정성장학회 2011 韓國結晶成長學會誌 Vol.21 No.6

삼척 도계지역의 탄광에서 석탄채취 시에 부산물로 발생되는 석탄폐석을 원료로 하여 제조된 분말유리와 다양한 종류의 발포제를 활용하여 발포유리를 제조하였다. 유리는 소다라임계 화학조성을 갖는 유리였고, 유리분말에 발포제로서 탄산칼슘, 인산칼슘, 그리고 석탄폐석 중 카본함량이 높은 셰일(shale) 계의 석탄폐석분말을 사용하였고, 이들 원료에 액상 바인더를 첨가하여 혼합한 후, 판상의 형태로 성형하였다. 성형체를 건조한 후 전기로에서 $800^{\circ}C$ 20분간 열처리함으로써 다공성의 발포유리 패널을 제조할 수 있었다. 발포제의 종류에 따라 다양한 특성을 갖는 발포유리샘플이 제조되었으며, 이들의 비중 및 압축강도와 같은 물리적 특성을 측정하였고, 기공의 크기 및 형태를 현미경으로 관찰하였다. 석탄폐석으로 제조한 폐유리를 활용하여 비중 0.4~0.7, 압축강도 30~72 kg/$cm^2$를 갖는 발포유리 샘플을 얻을 수 있었으며, 특히 액체인산 칼슘 발포제를 사용하여 0.47의 낮은 비중과 72 kg/$cm^2$의 높은 압축강도를 갖는 발포유리를 얻을 수 있었다. 따라서 삼척지역에 폐기된 다량의 석탄폐석이 건축용 및 산업용 발포유리 2차 제품을 제조하는데 충분히 활용이 가능하리라 판단되었다. Foamed glass was fabricated by using glass powder and foaming agents. For the glass powder, we used sodalime glass which's manufactured by using refused coal ore obtained as by-product from Dogye coal mine in Samcheok. And for the foaming agents, we used Calcium carbonate, Calcium phosphate and powder of shale type refused coal ore itself which has high content of carbon materials. We additionally used liquid binder for forming, and mixed together. And we formed rectangular shape and treated $800^{\circ}C$ for 20 min in an electrical furnace. The various kinds of foam glass samples were fabricated according to the kinds of foaming agents. The physical properties of samples, as specific gravity and compressive strength, were measured. Pore structure of each samples were investigated too. Foam glass with specific gravity of 0.4~0.7 and compressive strength of 30~72 kg/$cm^2$. Especially we get satisfying foam glass sample with low specific gravity of 0.47 and high compressive strength of 72 kg/$cm^2$ by the use of liquid calcium phosphate as foaming agent. It also had small and even shape of pore structure. Therefore, it is concluded that refused coal ore can be used for raw materials to manufacture secondary glass products such as a foamed glass panel for construction and industrial materials.

3계층 클라이언트/서버 구조를 가진 광역 번호안내시스템의 설계와 구현

임태영,유병규 한국통신학회 1998 한국통신학회 학술대회 및 강연회 Vol.1998 No.12