우상국,한인섭,김흥수,양준환,강을손,김종희 한국세라믹학회 1996 한국세라믹학회지 Vol.33 No.3
In the present study the effect of the addition of Fe on the pressureless and hot press sintering behavior was studied under Ar atmosphere. Pressureless sintering was performed 1900~220$0^{\circ}C$ under. Ar atmosphere. The addition of 1 wt% Fe was increased effectively of the sintered density. However it was impossible to obtain high density higher than 90%,. Zr-Fe-B compound in liquid phase was observed from the EDS and WDS analysis. It was considered that sinterability was enhanced due to the mass transfer through Fe based liquid phase formed at the sintering temperature. Hot pressing was performed at 1600~1$700^{\circ}C$ under Ar atmos-phere for 1 hr. It was possible obtain 95% relative density of ZrB2 specimen which is higher density at pressure-less sintering. It could be thought that ZrB2 particles was rearranged through liquid phase by applied pressure during initial stage of sintering.
졸-겔법을 이용하여 제조한 Al2O3-ZrO2 세라믹스에 미치는 하소온도의 영향
우상국,김종희 한국세라믹학회 1987 한국세라믹학회지 Vol.24 No.5
Characteristics of Al2O3-ZrO2 powders prepared by sol-gel process and their sintering behavior were investigated as a function of calcination temperature. The sol-gel processed powders were calcined at 800, 900, 1000, 1100, 1200$^{\circ}C$, and analyzed by X-ray diffraction technique. Pore size and distribution of green compact of the calcined powders were measured by mercury porosimeter. It is suggested that the optimal temperature of calcination for the sintering of Al2O3-ZrO2 powder prepared by sol-gel process is 1100$^{\circ}C$. In the Al2O3-17vol.% ZrO2 sintered specimen, which was sintered at 1600$^{\circ}C$ for 2hrs in air, 69vol.% tetragonal phse existed.