치과교정용 NiTi 합금계 선재의 탄성과 상변태 거동에 대한 열처리 효과
이진숙,김광만,김경남 대한치과기재학회 1997 대한치과재료학회지 Vol.24 No.1
Due to unique property of superelasticity, NiTi has been used widely since their introduction to the orthodontic specialty by Andreasen and Hillmann. But sufficent evaluation of superelasticity of domestic marketed wires has not yet been made. It has been known that heat treatment caused changes not only of elastic behavior but also of phase transformation behavior, an important factor of superelasticity. So, this study was investigated into varied ways of heat treatment of wires for orthodontic force proper for each clinical case. Each elastic behavior of 6 commercial NiTi alloy orthodontic arch wires(LG's ORTHOLLOY, G & H's Nickel Titanium arch wire, ORMCO's NI-TI and COPPER NI-TI, TOMY's SENTALLOY and 3M Unitek's Nitinol) were examined, and in order to study the effect of heat treatment on elasticity and phase transformation behavior, 3-point bending test, differential scanning calorimetry and X-ray diffraction with each wire heated at 350℃, 450℃ and 550℃ for 1hour were carried out compared with a as-recieved group. The results were as follows : 1. As a result of 3-point bending test in a control group, all wires had superelasticity and COPPER NI-TI showed the lowest maximum load as well as minimum(P<0.05). 2. As a result of 3-point bending est, except Nitinol and COPPER NI-TI, the wires in the group heated at 450℃ had lowest maximum and minimum load than that of a control group, and higher maximum and minimum load that of COPPER NI-TI in control group, and had superelasticity without and permanent deformation(P<0.05). 3. Phase transition temperature of all wires heated at 350℃ except COPPER NI-TI became higher but it became lower when they were heated at 450℃ and 550℃. 4. All wires in control group had austenite structure and when they were heated, martensite phase increased, and R phase appeared when heated at 550℃. The wires used in this study were changed in phase transition temperature, structure and elastic behavior as well by heat treatment. So this study showed that even the same kind of wire could be varied and used after heat treated, choosing proper load in accordance with each orthodontic clinic case.
RISS
DBpia연관 검색어 추천
이 검색어로 많이 본 자료
활용도 높은 자료