Yingguang Liang,Chunxiang Cui,Hongtao Geng,Lu Liu,Sen Cui,Shichao Yang 대한금속·재료학회 2023 METALS AND MATERIALS International Vol.29 No.4
In this work, as an inoculant, in-situ BaB6/Al composites was fabricated and used to refine the α-Al dendrites and modify theeutectic Si of A356.2(Al–7Si–0.3Mg) alloy. BaB6/Al ingot and ribbon composites mainly contain two phases, α-Al and BaB6. In BaB6/Al ribbons, nano-size BaB6ceramic particles exist and disperse uniformly which help to better exert the inoculanteffect in A356.2 alloy. YS, UTS, EL and HV of B2 alloy are 36.3%, 18.3%, 46.4% and 20.8% higher than the base alloy (B0),respectively. The ductile fracture characteristics are more obvious. Moreover, B2 alloy shows the best corrosion resistance. Aland BaB6form a clear, stable and well matched interface, so BaB6particles can act as the heterogeneous nucleation of α-Aland refine the A356.2 alloy. Furthermore, the combined of free micro-alloying elements Ba and B in BaB6/Al compositespromote the twins formation, which change the eutectic Si to fine fibrous and granular shape.