http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
The effect of different adhesive system applications on push-out bond strengths of glass fiber posts
Kivanc, Bagdagul Helvacioglu,Arisu, Hacer Deniz,Uctasli, Mine Betul,Okay, Tufan Can The Korean Academy of Prosthodonitics 2013 The Journal of Advanced Prosthodontics Vol.5 No.3
PURPOSE. Over the past years, the adhesion of fiber posts luted with simplified adhesive systems has been a matter of great interest. The aim of this study was to assess the post retentive potential of a self-adhesive resin cement using different adhesive systems to compare the push-out bond strengths of fiber posts. MATERIALS AND METHODS. The post spaces of 56 mandibular premolar roots were prepared and divided into 4 experimental groups and further divided into 2 subgroups according to testing time (n=7). The fiber posts (Rely X Fiber Post) were luted with a self-adhesive resin cement (RelyX Unicem) and one of the following adhesive systems: no adhesive, a total-etch adhesive resin (Single Bond), a two-step self-etch adhesive resin (Clearfil SE Bond) and a one-step self-etch adhesive resin (Clearfil S3 Bond). Each root was cut horizontally, and 1.5 mm thick six root segments were prepared. Push-out tests were performed after one week or three months (0.5 mm/min). Statistical analysis were performed with three-way ANOVA (${\alpha}$=.05). RESULTS. Cervical root segments showed higher bond strength values than middle segments. Adhesive application increased the bond strength. For one week group, the total-etch adhesive resin Single Bond showed higher bond strength than the self-adhesive resin cement RelyX Unicem applied without adhesive resin at middle region. For 3 months group, the two-step self-etch adhesive resin Clearfil SE Bond showed the highest bond strength for both regions. Regarding the time considered, Clearfil SE Bond 3 months group showed higher bond strength values than one week group. CONCLUSION. Using the adhesive resins in combination with the self-adhesive resin cement improves the bond strengths. The bond strength values of two-step self-etch adhesive resin Clearfil SE Bond improved as time passes.
Oguz, Ece Irem,Ozgur, Merve Erdog,Sungur, Sercan,Uctasli, Sadullah The Korean Academy of Prosthodonitics 2020 The Journal of Advanced Prosthodontics Vol.12 No.4
PURPOSE. The aim of this study was to evaluate the effect of multiple firings on the bond strength between yttriatetragonal zirconia polycrystals (Y-TZP) and 2 types of resin cements. MATERIALS AND METHODS. Sixty 3Y-TZP specimens (LAVA Frame Multi) were divided into 3 groups depending on the following firing procedures: (1) 2-firing cycles, (2) 5-firing cycles, (3) 10-firing cycles. Two samples from each group were investigated by using SEM to determine the morphological changes. All specimens were treated with 125 ㎛ airborne-particle abrasion and the surface roughness of each specimen was measured. The specimens from each firing group were then further divided into 2 subgroups (n = 9) to apply 2 types of resin cement (MDP-free resin cement: RelyX Unicem-RU, and MDP containing resin cement: Panavia F 2.0-PA). The shear bond strength (SBS) test was performed and failure types of all the debonded specimens were classified by using a stereomicroscope as adhesive, cohesive, and mixed. The statistical analysis of surface roughness and SBS data were performed by using 1-way ANOVA and 2-way ANOVA followed by Tukey-HSD tests (α=.05). Failure modes were calculated as a percentage for each group. RESULTS. The bond strength of RU and PA to the specimens obtained with 2 firings were not statistically different from each other (P=.1). However, the SBS values of PA were found to be significantly higher than RU for the specimens obtained with 5 and 10 firing cycles (P=.001 and P=.02, respectively). Surface roughness analysis revealed no statistical difference between groups (P=.2). The SEM analysis of samples fired 5- and 10- times showed irregularities and boundary loss in zirconia grains, and empty spaces between zirconia grains. CONCLUSION. The bond strength of PA cement was higher than that of RU to the zirconia subjected to repeated firings (5 and 10 firing cycles). When zirconia is subjected to multiple firings, using MDP-containing resin cement can be recommended.