Polymerization of Polyethylene Using Bimodal TiCl<sub>4</sub>/MgCl<sub>2</sub>/SBA-15/MCM-41
Moonyakmoon, Mattanawadee,Klinsrisuk, Sujitra,Poonsawat, Choosak Korean Association for Particle and Aerosol Resear 2015 Particle and Aerosol Research Vol.11 No.3
MCM-41 (Mobil Composition of Matter) and SBA-15 (Santa Barbara Amorphous) were used as a supported catalyst for ethylene polymerization due to their combination of large surface area and wide range of pore size distribution. The morphology of supports was used to control the morphology of the resulting polymer. Different molar ratios of Al/Ti were used for ethylene polymerization at $60^{\circ}C$ under atmospheric pressure. The effect of different mass ratios of MCM-41/SBA-15 and 1-hexene concentration on polymerization activity and polymer properties was investigated. The catalytic activity and the crystallinity reached the highest value at Al/Ti of 480. Upon incorporation of MCM-41 and SBA-15 into $MgCl_2/TiCl_4$ catalyst, the molecular weight and crystallinity of polyethylene were enhanced. The obtained polyethylene showed melting temperature between 130 and $135^{\circ}C$. The polyethylene with replication structure of support and bimodal MWD was expected.
Panpoom, Salinla,Klinsrisuk, Sujitra,Martwiset, Surangkhana,Poonsawat, Choosak Korean Association for Particle and Aerosol Resear 2015 Particle and Aerosol Research Vol.11 No.4
SBA-16 (Santa Barbara Amorphous) was synthesized over supported $TiCl_4/MgCl_2$. Due to its high surface area and excellent morphological performance, it was expected to form the bi-supported catalytic system and be used for ethylene polymerization. Polymerization of ethylene was carried out at atmospheric pressure using hexane as solvent and triethylaluminium as cocatalyst. ICP, FTIR, DSC, TG-DTA were used to characterize polyethylene and catalyst product. Optimum conditions for ethylene polymerization were found to be 100 mL hexane, Al/Ti molar ratio of 160 and 1 h polymerization at $60^{\circ}C$. The activity of 396.76 kg PE/mol Ti.h.atm was achieved. Melting point of the obtained polymer was in the range of $132-135^{\circ}C$ and the highest degree of crystallization was 46%.