Phase Transformation Behavior of Bi2O3-ZnO-Nb2O5 Ceramics sintered at low Temperature
Shiao Fu-Thang,Ke Han-Chou,Lee Ying-Chieh 한국분말야금학회 2006 한국분말야금학회 학술대회논문집 Vol.2006 No.1
To co-fire with commercial LTCC (Low Temperature Co-fired Ceramic) materials at , different contents of were added to the (BZN) ceramics. According to the test results, the cubic phase of BZN was transformed into orthorhombic in all the test materials. phase was formed in test materials with of addition. The phase transformation of cubic BZN was controlled during the synthesis process with excess ZnO content. The Cubic and orthorhombic phases of BZN could coexist and be sintered densely at .