Synthesis and Gas Adsorption Properties of Carbide-Derived Carbons from Titanium Tin Carbide
Yuanyuan Zhu,Aiguo Zhou,Jin Jia,Junjun Wang,Jiang Liu,Baolin Xing,Chuanxiang Zhang 성균관대학교(자연과학캠퍼스) 성균나노과학기술원 2016 NANO Vol.11 No.4
Here we reported the synthesis of nanoporous carbide-derived carbons (CDCs) from a new precursor, titanium tin carbides (Ti2SnC), via chlorination at 400–1100℃. At low chlorination temperature (400–500℃), as-synthesized CDCs mainly consisted of amorphous carbon and chlorides. As the chlorination temperature increased up to 600℃, chlorides disappeared, and the main composition of CDCs was amorphous carbon. At high chlorination temperature, there was a trend of graphitization. The microstructure of CDCs was observed and characterized by scanning electron microscopy and transmission electron microscopy. Some graphite-like sheet structures in CDCs were found. Specific surface area (SSA) and pore volume of CDCs increased with chlorination temperature, except an abnormal decrease of the CDC chlorinated at 900℃. CDC chlorinated at 1100℃ had the largest SSA, 1580 m2 /g. In order to apply these materials as novel hydrogen/methane storage media in the area of energy efficient transport, gas adsorption properties of CDCs were measured. For CDC chlorinated at 1100℃, pore volume uptakes are 206 cm3 /g at 60 bar (25℃) for methane, and ~442 cm3 /g at 35 bar (-196℃) for hydrogen, respectively. It was suggested that CDCs from Ti2SnC are promising materials for hydrogen/ methane adsorptive storage.