다이캐스팅 공정에 사용된 개량형 STD61 열간 금형 표면의 미세조직에 관한 연구
유하영 ( Ha-young Yu ),이승준 ( Seung-joon Lee ),강민우 ( Min Woo Kang ),이석진 ( Suk-jin Lee ),양원존 ( Won Jon Yang ),정재석 ( Jae Suk Jeong ),김병훈 ( Byung-hoon Kim ),이영국 ( Young-kook Lee ) 대한금속재료학회(구 대한금속학회) 2016 대한금속·재료학회지 Vol.54 No.9
The surface microstructure and crack formation of an aluminum die-casting mold were investigated. The mold was made of a modified STD61 steel, and was used for more than 165,000 cycles. The mold surface consisted of four layers; an oxidized layer, a decarburized layer, a network carbide layer and a tempered martensite matrix. The depth down to the hardest network carbide layer was ~200 μm. Inside the matrix, M3C transition carbides were dissolved so that solute C joined pre-existing M23C6 and MC carbides to make them coarse. About 60% of thermal fatigue cracks had a depth less than 200 μm due to the hard network carbide layer, which obstructed the propagation of cracks. Cracks of over 200 μm were filled with oxide wedges of Al and Si which was which flown from the molten alloy as well as the Fe oxide.(Received March 2, 2016; Accepted April 7, 2016)