산소분리를 위한 Ba0.5Sr0.5Co0.8Fe0.2O3-δ 관형 분리막 제조 및 투과 특성
김종표 ( Jong Pyo Kim ),손수환 ( Sou Hwan Son ),박정훈 ( Jung Hoon Park ),이용택 ( Yong Taek Lee ) 한국화학공학회 2011 Korean Chemical Engineering Research(HWAHAK KONGHA Vol.49 No.6
Tubular Ba0.5Sr0.5Co0.8Fe0.2O3-δ membranes were prepared by extrusion. TGA results of green body membrane after extrusion showed three successive weight losses due to decomposition of organic additives and carbonate. Drying shrinkage rate of tubular Ba0.5Sr0.5Co0.8Fe0.2O3-δ membranes was no change after 68 h and higher in the membrane with large outer diameter. XRD and SEM results showed the sintered membranes were the single phase structure and dense. The stoichiometric molar ratio agreed well with composition ratio calculated by EDS results for Ba0.5Sr0.5Co0.8Fe0.2O3-δ membrane. Radial crushing strength of tubular Ba0.5Sr0.5Co0.8Fe0.2O3-δ membrane with 0.95 mm thickness was 5.7 kgf /mm2 and the oxygen permeation rate of same membrane was 146.85 mL/min (Jo2=2.33 mL/min·cm2) at 950 ℃. Therefore, it was known that use of vacuum pump was more effective than that of sweep gas to obtain higher oxygen permeation flux.