http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
나기백(Gi-Baek Nah),류지애(Ji-Ae Ryu),이중명(Jung-Myoung Lee),엄태진(Tae-Jin Eom) 한국펄프·종이공학회 2017 펄프.종이技術 Vol.49 No.4
As a basic study for the new materialization of biomass, the chemical dispersion of biomass using microwave was performed under various conditions. And the characteristics of dispersed residues were compared with various conditions. According to the reaction condition of microwave, the residual ratio by chemical micronization of wood meals was decreased, and Klason lignin of residues were also decreased. However, the content of acid soluble lignin did not show any significant difference. These results indicate that the chemical dispersion reaction using microwave showed the lowest residual lignin content at 60 seconds of reaction time and 2.5% of the catalyst condition or at 120 seconds and 2.0%. It is expected that the residual ratio and the residual lignin content can be controlled by the catalyst content and reaction time in the chemical micronization.
Glycol Ether를 이용한 국내산 참나무류의 LAS 펄프화
김강재(Kang-Jae Kim),나기백(Gi-Baek Nah),류지애(Ji-Ae Ryu),엄태진(Tae-Jin Eom) 한국펄프·종이공학회 2018 펄프.종이技術 Vol.50 No.2
The pulp from Korean mixed oaks were prepared by LAS (Low temperature, Atmospheric pressure, and Short reaction time) pulping method with different temperature and reaction. The pulp prepared under low cooking temperature had a high residual lignin content spite of increasing cooking time. However, as the cooking temperature increased, the lignin in the wood was easily removed and the yield of pulp increased and the residual lignin content decreased. The peak intensities derived from hemicellulose and lignin, which have been confirmed from wood chips, are gradually weaker in response to pulping. Peak regions representing cellulose were strongly confirmed from IR data of pulp prepared at more than 110℃. It can be concluded that pulping of Korean mixed oak was suitable for 60 minutes at 110℃. It was predicted that the possibility of using the LAS pulp as a raw material for papermaking was high because the LAS pulp showed the same fiber characteristics as KP. LAS pulp showed higher glucose content than wood chip, many hemicellulose was eluted by acid catalyst and showed low xylose content. The reason why the syringaldehyde ratio of LAS pulp decreased compared to wood chips was that a large amount of lignin was condensed by cooking reaction.
화학적 미분화에 의한 리그닌이 풍부한 마이크로셀룰로오스 미세분의 제조 및 수초 특성
김강재(Kang-Jae Kim),나기백(Gi-Baek Nah),류지애(Ji-Ae Ryu),엄태진(Tae-Jin Eom) 한국펄프·종이공학회 2017 펄프.종이技術 Vol.49 No.3
In this study, chemical micronization method was used to produce (lignin rich microcellulose fines (LMCFs) of 10% lignin contents. The handsheets of containing 5% LMCFs were prepared and analyzed their physical characteristics. The morphology of LMCFs were changed according to the grinder (Super Masscollider) passing number. After passing 10 times through the grinder, the shape of LMCFs became similar to those of secondary fines. The drainage time of LMCFs was much shorter than that of MFCs. The tensile index gradually increased with the grinding passing number of LMCFs. The tensile index of the handsheet containing LMCFs of 10 passing number was 38.8 N·m/g, that was 33% improvement from the handsheet without LMCFs. The brightness of the handsheet containing LMCFs was improved in proportional to the grinder passing number.