김철위,Kim, Cheol-We 대한치과보철학회 1978 대한치과보철학회지 Vol.16 No.1
The object of this study was to measure of the distortion of various dental waxes under condition simulating clinical usage. Eleven commercial product (table) including the inlay and baseplate waxes were tested, and compared in the study. Test specimens were prepared $5{\times}5{\times}65mm$. split brass mold. Placed this rod wax specimens and the brass wax distortion test mold into the water bath and tested the distortion values for waxes at $35^{\circ}C,\;40^{\cric}C,\;45^{\circ}C\;and\;50^{\circ}C$. Measured the distortion as the difference between the final (Df) and original (Do) distance between the ends of the specimen. Recorded Df, Do and Df-Do (Distortion) to the nearest 0.5mm. A minimum of five specimens were tested for each material. The following conclusions may be drawn from this study. 1) It can be seen that, a significant wax distortion was obtained with the temperature of forming the pattern, and the length of time and the temperature at which it was stored. 2) It was found that, when the storage time was increased, the wax distortion was correspondingly increased. At the sametime, the higher the storage time was employed, the distortion was obviously much greater. 3) It can be observed that the higher the temperature at which the wax was manipulated, the less was the resulting distortion upon storage.