Corrosion Fatigue of Austenitic Stainless Steel in Different Hot Chloride Solutions
( A. Visser ),( G. Mori ),( M. Panzenbock ),( R. Pippan ) 한국부식방식학회 2015 Corrosion Science and Technology Vol.14 No.4
Austenitic stainless steel was investigated under cyclic loading in electrolytes with different chloride contents and pH and at different temperatures. The testing solutions were 13.2 % NaCl (80,000 ppm Cl-) at 80 ¡ÆC and 43 % CaCl2 (275,000 ppm Cl-) at 120 ¡ÆC. In addition to S.N curves in inert and corrosive media, the fracture surfaces were investigated with a scanning electron microscope (SEM) to analyse the type of attack. The experimental results showed that a sharp decrease in corrosion fatigue properties can be correlated with the occurrence of stress corrosion cracking. The correlation of occurring types of damage in different corrosion systems is described.