<▼1><B>Abstract</B><P/></▼1><▼2><P>Thick coatings of tetrahedral amorphous carbon (ta-C) have great existing and potential commercial importance for components such as automobile accessories. We confirme...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107641955
2016
-
SCOPUS,SCIE
학술저널
1957-1963(7쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<▼1><B>Abstract</B><P/></▼1><▼2><P>Thick coatings of tetrahedral amorphous carbon (ta-C) have great existing and potential commercial importance for components such as automobile accessories. We confirme...
<▼1><B>Abstract</B><P/></▼1><▼2><P>Thick coatings of tetrahedral amorphous carbon (ta-C) have great existing and potential commercial importance for components such as automobile accessories. We confirmed the feasibility of depositing thick ta-C coating on Si wafer, WC, stainless steel (STS), and Al alloy substrates by a home-made filtered cathode vacuum arc. A ta-C coating of 800 nm thickness was successfully deposited over 20 min continuous coating. Interestingly, coatings with thicknesses exceeding 1 μm were easily delaminated by thermal and internal stress effects when the coating time exceeded 20 min. Varying the bias (0 V ↔ 500 V) was highly effective in controlling the internal stress relaxation of the ta-C. This method showed significant improvements in the stress relaxation of the ta-C coatings. By applying multicycle coating, the thickness and hardness of the ta-C coating could reach 9.3 μm and 45 GPa, respectively, at a coating speed of 3.0 μm/h on a fixed substrate.</P></▼2>