종자 결정 성장법으로 제조된 $GdBa_2Cu_3O_{7-y}$ 벌크 초전도체의 자기적 특성 = Magnetic Properties of $GdBa_2Cu_3O_{7-y}$ Bulk Superconductors Fabricated by a Top-seeded Melt Growth Process

다국어 초록 (Multilingual Abstract)

The fabrications condition and superconducting properties of top-seeded melt growth (TSMG) processed $GdBa_2Cu_3O_{7-y}$ (Gd123) bulk superconductors were studied. Processing parameters (a maximum temperature ($T_{max}$), a temperature for crystal growth ($T_G$) and a cooling rate ($R_G$) through a peritectic temperature ($T_P$) for the fabrication of single grain Gd123 superconductors were optimized. The magnetic levitation forces, trapped magnetic fields, superconducting transition temperature ($T_c$) and critical current density ($J_c$) of the Gd123 bulks superconductors were estimated. Single grain Gd123 bulk superconductors were successfully fabricated at the optimized processing condition. The $T_c$ of a TSMG processed Gd123 sample was 92.5 K and the $J_c$ at 77 K and 0 T was approximately $50kA/cm^2$. The trapped magnetic field contour and magnetic levitation forces were dependent on the top surface morphology of TSMG processed Gd123 samples. The single grain Gd123 samples, field-cooled at 77 K using a Nd-B-Fe permanent magnet with 5.27 kG and 30 mm dia., showed the trapped magnetic field contour of a single grain with a maximum of 4 kG at the sample center. The maximum magnetic levitation forces of the single grain Gd123 sample, field-cooled or zero field-cooled, were 40 N and 107 N, respectively.

참고문헌 (Reference)

1 M. Ikeda, 469 : 1270-, 2009

2 C. Xu, 18 : 229-, 2005

3 U. Mizutani, 13 : 863-, 2000

4 M. Morita, 733-, 1991

5 W. Lo, 11 : 786-, 1996

6 P. Schätzle, 12 : 1999-, 1999

7 Y. A. Jee, 13 : 2000-, 195

8 C. J. Kim, 357 : 635-, 2001

9 C. J. Kim, 10 : 947-, 1997

10 D. A. Cardwell, 445 : 1-, 2006

11 S. Nariki, 13 : 778-, 2000

12 S. Nariki, 357 : 811-, 2001

13 C. J. Kim, 8 : 652-, 1995

14 C. J. Kim, 11 : 831-, 1992

15 H. Hinai, 357 : 706-, 2001

16 C. Xu, 426 : 613-, 2005

17 T. Oka, 470 : 1799-, 2010