Port facilities and marine structures used in marine environment were encountered to corrosion damages because of the influence of CI-. Generally, to protect these accidents, mainly applied anti-corrosion paint and epoxy coating. But it was still rema...
Port facilities and marine structures used in marine environment were encountered to corrosion damages because of the influence of CI-. Generally, to protect these accidents, mainly applied anti-corrosion paint and epoxy coating. But it was still remained erosion-corrosion damage such as impingement erosion, cavitation erosion, deposit attack. There was needs to develope the new coating materials to protective those corrosion damages.<br/>
This paper, polyester glass flake, vinylester glass flake lining and epoxy coating for SS400 were investigated electrochemical tests and cavitation erosion test for corrosion behaviour under sea water.<br/>
The main results obtained are as follows ;<br/>
1) Surface of epoxy coating appear erosion pin hole but surface of polyester glass flake and vinylester glass flake lining do not appear erosion pin hole after impingement-cavitation erosion test in sea water.<br/>
2) Weight loss of polyester glass flake and vinylester glass flake lining do not occur after impingement-cavitaton erosion test in sea water.<br/>
3) Corrosion current density of polyester glass flake lining less drained than epoxy coating and substrate under corrosion potential..<br/>
4) Corrosion current density of vinylester glass flake lining with three coating less drained than that of polyester glass flake lining with two coating.