Antifatigue failure technology take an important the part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. In this study, the influence of shot ...
Antifatigue failure technology take an important the part of current industries. Currently, the shot peening is used for removing the defect from the surface of steel and improving the fatigue strength on surface. In this study, the influence of shot peening and corrosive condition for corrosion property was investigated on immersed in 3.5% NaCl, 10% HN03 + 3% HF, 6% FeC13. The immersion test was performed on two kind of specimen. The immersion periods was performed 90days. Corrosion potential, weight loss were investigated from experimental results.