Zinc Oxide(ZnO) thin films on Si(100) substrate were deposited by RF magnetron reactive sputtering. The charcteristics of ZnO thin films on argon/oxygen(Ar/O$_2$)gas ratios RF power and substrate temperature were investigated by XRD, SEM, and AFM analyses. C-axis preferred orientation resistivity and surface roughness highly depended on Ar/O$_2$gas ratios. The resistivity of ZnO thin films rapidly increased with increasing oxygen ratio and the resistivity value of 9$\times$10$^{7}$ $\Omega$cm was obtained at a working pressure of 10 mTorr with Ar/O$_2$=50/50. The surface roughness was also improved with increasing oxygen ratio and the ZnO films deposited with Ar/O$_2$=50/50 showed the excellent roughness value of 28.7$\AA$.