Hemicelluloses are useful materials for papermaking and other biotechnological applications. Based on the concept of transformation of a chemical pulp mill into an integrated forest biorefinery, hemicelluloses are partially extracted or separated, and the remained substrate (mainly cellulose and lignin) can be further delignified for pulp. In the present work, the parameters of pre-extraction or the effect on pulp properties was investigated. The hot-water extraction and alkaline extraction prior to kraft pulping of poplar were carried out in order to partially extract hemicelluloses. It was found that the hot water extraction can obtain a mass loss of 7.72% at 140℃ for 60 min with a water-to-wood ratio of 6:1, and mass loss of woodchips increased with extraction time and temperature. While in the alkaline extraction, mass loss of woodchips reached 15.20% at 170℃ for 120 min with 3% dosage of NaOH. The concentrations of sugars depolymerized from hemicellulose in extraction liquor increased with the increase of extraction time and temperature. The residual woodchips were subjected to kraft pulping at 165℃ for 60 min with 20% effective alkali, 25% sulfidity and a liquor-to-wood ratio of 4:1. Considering the needs for resulting pulp properties, a temperature of 140℃ and a pre-extraction time of 60 min without NaOH addition were recommended as the optimum pre-extraction in this experiment.

목차 (Table of Contents)

ABSTRACT
1. Introduction
2. Materials and Methods
3. Results and Discussion
4. Conclusions

ABSTRACT
1. Introduction
2. Materials and Methods
3. Results and Discussion
4. Conclusions
Literature Cited

참고문헌 (Reference)

1 조휘, "열수 및 알칼리 용액을 이용한 국산 목재 칩으로부터 헤미셀룰로오스의 선추출 및 특성 구명" 한국펄프·종이공학회 43 (43): 83-91, 2011

2 서동일, "열수 및 알칼리 용액을 이용하여 국산 목재 칩으로부터 선추출한 헤미셀룰로오스의 특성과 이에 따른 수초지 물성 변화" 한국펄프·종이공학회 43 (43): 60-67, 2011

3 Ebringerová, A., "Xylan and xylan derivatives - biopolymers with valuable properties. 1. naturally occurring xylans structures, isolation procedures and properties" 21 (21): 542-556, 2000

4 Cvt, M., "Valorisation of hardwood hemicelluloses in the kraft pulping process by using an integrated biorefinery concept" 87 (87): 197-207, 2009

5 Miller, G. L., "Use of dinitrosalicylic acid reagent for determination of reducing sugar" 31 (31): 426-428, 1959

6 Yang, G., "Recovery of acetic acid from prehydrolysis liquor of hardwood kraft-based dissolving pulp production process by reactive extraction with triisooctylamine" 138 (138): 253-, 2013

7 Al-Dajani, W. W., "Preextraction of hemicelluloses and subsequent kraft pulping part I: alkaline extraction" 7 : 3-8, 2008

8 Walton, S. L., "Pre-extraction of hemicelluloses from hardwood chips using an alkaline wood pulping solution followed by kraft pulping of the extracted wood chips" 49 (49): 12638-12645, 2010

9 Yang, G., "Influence of the diluent on the extraction of acetic acid from the prehydrolysis liquor of kraft based dissolving pulp production process by tertiary amine" 120 (120): 341-345, 2013

10 Helmerius, J., "Impact of hemicellulose pre-extraction for bioconversion on birch kraft pulp properties" 101 (101): 5996-6005, 2010