고강도 방탄소재를 위한 Borosilicate 유리의 결정화 = Crystallization of Borosilicate Glasses for High-Strength Bulletproof Materials

다국어 초록 (Multilingual Abstract)

Borosilicate glass(GVB-Solutions in glass, 2mm, Germany) was prepared in the composition of $80.4SiO_2-4.2Na_2O-2.4Al_2O_3-13.0B_2O_3$. The 2-step crystallization was performed around $584^{\circ}C$ of glass transition temperature ($T_g$), and $774^{\circ}C$ of crystallization temperature($T_c$). The maximum nucleation rate was $8.8{\time}10^9/mm^3{\cdot}hr$ at $600^{\circ}C$ and the maximum crystal growth rate was 3.5nm/min at $750^{\circ}C$. The maximum mechanical properties were observed at 22.8% of volume fraction, the strength, hardness and fracture toughness was 555MPa, $752kg/mm^2$, $1.082MPa{\cdot}mm^{1/2}$. The crystal size of 177nm which has volume fraction of 22.8% showed maximum strength of 562MPa, it is about 157% higher than parent borosilicate glass. From these results, the crystallized borosilicate glass can be applied weight lighting of bullet proof materials.

참고문헌 (Reference)

1 S. W. Freiman, 55 : 1972

2 P. Hing, (8) : 1041-, 1973

3 P. W. Mcmillan, (1) : 269-, 1966

4 심규인, "방탄소재 활용을 위한 SLS 유리 결정화의 효과" 한국군사과학기술학회 13 (13): 120-125, 2010

5 Choi, S. Y, "Workshop Report of 2nd stage, Nano Technology Application Center" Agency for Defense Development 2011

6 Krauthammer, T, "Response of Reinforced Concrete Structural Elements to Severe Impulsive Loads" 53 (53): 119-130, 1994

7 Choi, S. Y, "Research & Development Report of 1st Stage" Nano Technology Application Center 2010

8 Mathieu Roskosz, "Kinetic vs. Thermodynamic Control of Crystal Nucleation and Growth in Molten Silicates" 352 : 180-184, 2006

9 S. Y. Choi, "Influence of Crystallization on Some Properties of ZrF4 - BaF2 - YF3 - AlF3 Glasses" 129 : 133-136, 1991

10 W. Holand, "Glass-Ceramics Biocompatible and Bioactive Glass-Ceramics-State of the Art and New Directions" 219 : 192-197, 1997

11 F. Wooten, "Electric Field Breakdown in Borosilicate Glass and Other Amorphous Insulators" 55 (55): 255-256, 1975

12 Song S-M, "Crystallization Property Effects in Ge30Se60 Te10 Glass" 217 (217): 79-82, 1997

13 Sung-Bum Sohn, "Crystallization Behavior in the Glass System MgO - Al2O3 - SiO2 : Influence of CeO2 Addition" 282 (282): 221-227, 2001

14 Sung-Bum Sohn, "Controlled Crystallization and Characterization of Cordierite Glass-Ceramics for Magnetic Memory Disk Substrate" 35 (35): 4815-4821, 2000

15 Krauthammer, T, "Blast Mitigation Technologies : Developments and Numerical Considerations for Behavior Assessment and Design" 5 : 1-12, 1998