The effect of coloring liquids on the translucency of zirconia framework
Tuncel, Ilkin,Eroglu, Erdal,Sari, Tugrul,Usumez, Aslihan The Korean Academy of Prosthodonitics 2013 The Journal of Advanced Prosthodontics Vol.5 No.4
PURPOSE. Translucency of all-ceramic restorations is an important factor which affects the final appearance and esthetic outcome of the restoration. The aim of this study was to evaluate the effect of the shade of coloring liquid on the translucency of zirconia framework. MATERIALS AND METHODS. Thirty zirconium oxide core plate ($15{\times}12{\times}0.5$ mm) were divided into 6 groups of 5 plates each. Each group was classified according to the shade of coloring liquid based on Vita Classic Scale (A2, A3, B1, C2, and D2), and each sample was immersed in coloring liquid for 3 seconds as recommended by the manufacturer, except for the control group. Contrast ratio, as a translucency parameter, was calculated using a spectrophotometer and the data were analyzed with oneway analysis of variance (ANOVA) and Tukey's honestly significant differences (HSD) tests (${\alpha}$=.05). RESULTS. Significant differences in translucency among the control and test groups, and the B1 shaded group and other shades was observed. There were no significant differences among A2, A3, C2, and D2 shaded groups. CONCLUSION. The translucency of the zirconium oxide cores was affected by the coloring procedure and significant differences in the translucency measurements were identified between specific shades.
-
The effect of coloring liquids on the translucency of zirconia framework
Tugrul Sari,Erdal Eroglu,Aslihan Usumez,Ilkin Tuncel 대한치과보철학회 2013 The Journal of Advanced Prosthodontics Vol.5 No.4
PURPOSE Translucency of all-ceramic restorations is an important factor which affects the final appearance and esthetic outcome of the restoration. The aim of this study was to evaluate the effect of the shade of coloring liquid on the translucency of zirconia framework. MATERIALS AND METHODS Thirty zirconium oxide core plate (15 × 12 × 0.5 mm) were divided into 6 groups of 5 plates each. Each group was classified according to the shade of coloring liquid based on Vita Classic Scale (A2, A3, B1, C2, and D2), and each sample was immersed in coloring liquid for 3 seconds as recommended by the manufacturer, except for the control group. Contrast ratio, as a translucency parameter, was calculated using a spectrophotometer and the data were analyzed with oneway analysis of variance (ANOVA) and Tukey's honestly significant differences (HSD) tests (α=.05). RESULTS Significant differences in translucency among the control and test groups, and the B1 shaded group and other shades was observed. There were no significant differences among A2, A3, C2, and D2 shaded groups. CONCLUSION The translucency of the zirconium oxide cores was affected by the coloring procedure and significant differences in the translucency measurements were identified between specific shades.
-
Evaluation of the bond strength between aged composite cores and luting agent
Caner Ozturk,Alirıza Tuncdemir,Aslıhan usumez,Fatma Cebe,Serdar Polat 대한치과보철학회 2015 The Journal of Advanced Prosthodontics Vol.7 No.2
PURPOSE The aim of this study was to evaluate effect of different surface treatment methods on the bond strength between aged composite-resin core and luting agent. MATERIALS AND METHODS Seventy-five resin composites and also seventy-five zirconia ceramic discs were prepared. 60 composite samples were exposed to thermal aging (10,000 cycles, 5 to 55℃) and different surface treatment. All specimens were separated into 5 groups (n=15): 1) Intact specimens 2) Thermal aging-air polishing 3) Thermal aging- Er:YAG laser irradiation 4) Thermal aging- acid etching 5) Thermal-aging. All specimens were bonded to the zirconia discs with resin cement and fixed to universal testing machine and bond strength testing loaded to failure with a crosshead speed of 0.5 mm/min. The fractured surface was classified as adhesive failure, cohesive failure and adhesive-cohesive failure. The bond strength data was statistically compared by the Kruskal-Wallis method complemented by the Bonferroni correction Mann-Whitney U test. The probability level for statistical significance was set at α=.05. RESULTS Thermal aging and different surface treatment methods have significant effect on the bond strength between composite-resin cores and luting-agent (P<.05). The mean baseline bond strength values ranged between 7.07 ± 2.11 and 26.05 ± 6.53 N. The highest bond strength of 26.05 ± 6.53 N was obtained with Group 3. Group 5 showed the lowest value of bond strength. CONCLUSION Appropriate surface treatment method should be applied to aged composite resin cores or aged-composites restorations should be replaced for the optimal bond strength and the clinical success.
-
Evaluation of the bond strength between aged composite cores and luting agent
Polat, Serdar,Cebe, Fatma,Tuncdemir, Aliriza,Ozturk, Caner,Usumez, Aslihan The Korean Academy of Prosthodonitics 2015 The Journal of Advanced Prosthodontics Vol.7 No.2
PURPOSE. The aim of this study was to evaluate effect of different surface treatment methods on the bond strength between aged composite-resin core and luting agent. MATERIALS AND METHODS. Seventy-five resin composites and also seventy-five zirconia ceramic discs were prepared. 60 composite samples were exposed to thermal aging (10,000 cycles, 5 to $55^{\circ}C$) and different surface treatment. All specimens were separated into 5 groups (n=15): 1) Intact specimens 2) Thermal aging-air polishing 3) Thermal aging- Er:YAG laser irradiation 4) Thermal aging- acid etching 5) Thermal-aging. All specimens were bonded to the zirconia discs with resin cement and fixed to universal testing machine and bond strength testing loaded to failure with a crosshead speed of 0.5 mm/min. The fractured surface was classified as adhesive failure, cohesive failure and adhesive-cohesive failure. The bond strength data was statistically compared by the Kruskal-Wallis method complemented by the Bonferroni correction Mann-Whitney U test. The probability level for statistical significance was set at ${\alpha}$=.05. RESULTS. Thermal aging and different surface treatment methods have significant effect on the bond strength between composite-resin cores and luting-agent (P<.05). The mean baseline bond strength values ranged between $7.07{\pm}2.11$ and $26.05{\pm}6.53$ N. The highest bond strength of $26.05{\pm}6.53$ N was obtained with Group 3. Group 5 showed the lowest value of bond strength. CONCLUSION. Appropriate surface treatment method should be applied to aged composite resin cores or aged-composites restorations should be replaced for the optimal bond strength and the clinical success.