Effect of Acid Etching on Surface Chemistry and Microstructure of HA and CMP Grit-Blasted Ti Surface
Haryadi, A.W.,You, Chang Kuk,Kim, Shin Yoon,Park, Eui Kyun,Kim, Kyo Han,Kim, Suk Young Trans Tech Publications, Ltd. 2006 Key Engineering Materials Vol.309 No.-
<P>Grit blasting using bioactive HA and biodegradable CMP followed by acid etching has been done. HNO3 and H3PO4 were used for the etching solution by controlling the concentration and etching time to know the effect on the surface chemistry and morphology of the Ti implant. Characterization of samples was done by using SEM, EDX and surface profilometer. The contents of residues on Ti surface decreased with increasing acid concentration and etching time. It was observed that the acidic etching rate of HA grits on Ti surface was faster than that of CMP grits. And HNO3 etched more rapidly the HA and CMP grits on Ti surface, compared to H3PO4. Therefore, the surface roughness of dental implants can be controlled by having appropriate combination of acid concentration and etching time.</P>
Gunawan Dwi Haryadi,김선진 대한기계학회 2011 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.25 No.9
The present study evaluates the influences of PWHT on FCG behavior and tensile properties of TIG butt welded Al 6013-T4 sheets. Crack propagation tests were carried out on compact tension (CT) specimens. The T82 heat treatment was varied in three artificial aging times (soaking) of 6, 18 and 24 hours. The results of T82 heat treatment with artificial aging variations were tested for their fatigue crack growth rates at the main metal zone, the heat-affected zone (HAZ), and the welded metal zone. It has been observed that the various agings in heat treatment T82 are sensitive to the mechanical properties (fatigue crack growth rate test, tensile test). The results show that PWHT-T82 for 18 hours aging is the highest fatigue resistance, while the aging 18 hours provided the highest tensile test result.