Shear bond strengths of aged and non-aged CAD/CAM materials after different surface treatments
Hamiyet Kilinc,Fatma Ayse Sanal,Sedanur Turgut 대한치과보철학회 2020 The Journal of Advanced Prosthodontics Vol.12 No.5
PURPOSE. To assess shear bond strengths (SBS) of resin composites on aged and non-aged prosthetic materials with various surface treatments. MATERIALS AND METHODS. Cerasmart (CE), Vita Enamic (VE), Vita Mark II (VM), and IPS e.max CAD (EC) blocks were sliced, and rectangular-shaped specimens (14 × 12 × 1.5 mm; N = 352) were obtained. Half of the specimens were aged (5000 thermal cycles) for each material. Non-aged and aged specimens were divided into 4 groups according to the surface treatments (control, air abrasion, etching, and laser irradiation; n = 11) and processed for scanning electron microscopy (SEM). The repair procedure was performed after the surface treatments. SBS values and failure types were determined. Obtained data were statistically analyzed (P≤.05). RESULTS. The material type, surface treatment type, and their interactions were found significant with regard to SBS (P<.001). Aging also had a significant effect on prosthetic material-resin composite bonding (P<.001). SBS values of non-aged specimens ranged from 12.16 to 17.91 MPa, while SBS values of aged specimens ranged from 9.46 to 15.61 MPa. Non-aged VM in combination with acid etching presented the highest score while the control group of aged CE showed the lowest. CONCLUSION. Etching was more effective in achieving durable SBS for VM and EC. Laser irradiation could be considered as an alternative surface treatment method to air abrasion for all tested materials. Aging had significant effect on SBS values generated between tested materials and resin composite.
-
Effect of abutment types and resin cements on the esthetics of implant-supported restorations
Asena Çeken,Hamiyet Kılınç,Sedanur Turgut 대한치과보철학회 2023 The Journal of Advanced Prosthodontics Vol.15 No.3
PURPOSE. The aim of the study was to evaluate the optical properties of new generation (3Y-TZP) monolithic zirconia (MZ) with different abutment types and resin cement shades. MATERIALS AND METHODS. A1/LT MZ specimens were prepared (10 × 12 × 1 mm, N = 30) and divided into 3 groups according to cement shades as transparent (Tr), yellow (Y) and opaque (O). Abutment specimens were obtained from 4 different materials including zirconia (Group Z), hybrid (Group H), titanium (Group T) and anodized yellow titanium (Group AT). MZ and abutment specimens were then cemented. L*, a*, and b* parameters were obtained from MZ, MZ + abutment, and MZ + abutment + cement. ΔE001* (between MZ and MZ + abutment), ΔE002* (between MZ and MZ + abutment + cement) and ΔE003* (between MZ + abutment and MZ + abutment + cement) values were calculated. Statistical analyses included 2-way ANOVA, Bonferroni, and Paired Sample t -Tests (P < .05). RESULTS. Abutment types and resin cements had significant effect on L*, a*, b*, ΔE001*, ΔE002*, and ΔE003* values (P < .001). Without cementation, whereas zirconia abutment resulted in the least discoloration (ΔE001* = 0.68), titanium abutment caused the most discoloration (ΔE001* = 4.99). The least ΔE002* = 0.68 value was seen using zirconia abutment after cementation with yellow shaded cement. Opaque shaded cement caused the most color change (ΔE003* = 5.24). Cement application increased the L* values in all groups. CONCLUSION. The least color change with/without cement was observed in crown configurations created with zirconia abutments. Zirconia and hybrid abutments produced significantly lower ΔE002* and ΔE003* values in combination with yellow shaded cement. The usage of opaque shaded cement in titanium/anodized titanium groups may enable the clinically unacceptable ΔE00* value to reach the acceptable level.