물유리의 수분 함량 및 열처리 온도에 따른 다공체의 특성
공양표,서상훈,김종호,서동수,Kong, Yang-Pyo,Seo, Sang-Hun,Kim, Jong-Ho,Suhr, Dong-Soo 한국세라믹학회 2005 한국세라믹학회지 Vol.42 No.10
Porous ceramics which have closes pore were fabricated by heat treatment at 100$\∼$ 600$^{\circ}C$ for 30 min using dried water glasses with 25, 35, and 45 wt$\%$ water contents. Size and distribution of the closed pore were varied depending on the water contents and heat treatment temperature. The expansion procedure could be distinguished by two stages. The frist stage occurred around loo$\%$ due to the evaporation of water and the second stage occurred at 200$\∼$400$^{\circ}C$ due to the decomposition of Si-OH compounds. The specimen was not expanded successfully because of the softening of the dried water glass at 500$\∼$600$^{\circ}C$.
공양표,조호연,서동수,Kong, Yang-Pyo,Cho, Ho-Yeon,Suhr, Dong-Soo 한국세라믹학회 2008 한국세라믹학회지 Vol.45 No.1
Hydrated sodium silicate with 25 wt% water contents was synthesized by hydrothermal reaction using anhydrous sodium silicate. The hydrated sodium silicate was expanded at $370^{\circ}C$ for 30 min. and then pulverized, classified (- 200 mesh) and press-formed. The samples were heat treated at $400{\sim}900^{\circ}C$ for 30 min. in order to study the expansion characteristics depending on heat treatment temperature. A porous body with closed pore was formed above $600^{\circ}C$. The volume expansion ratio and the pore size were increased and the specific gravity was decreased with increasing heat treatment temperature. However, the volume expansion ratio was decreased and the specific gravity was increased above $850^{\circ}C$ due to the softening of the sodium silicate.
공양표,조호연,서동수,Kong, Yang-Pyo,Cho, Ho-Yeon,Suhr, Dong-Soo 한국세라믹학회 2008 한국세라믹학회지 Vol.45 No.3
In order to fabricate porous ceramics, hydrated sodium silicate was synthesized by hydrothermal reaction using anhydrous sodium silicate. The microstructural and the structural characteristics of the expanded ceramics were observed depending on heat treatment temperature (550, 600, 650, $700^{\circ}C$) and then the effect of these characteristics on the compressive strength and the temperature gradient was investigated. As the heat treatment temperature was increased, the compressive strength was decreased from $0.717KN/cm^2\;(550^{\circ}C)\;to\;0.166KN/cm^2\;(700^{\circ}C)$. The temperature gradient was increased with increasing the experimental temperature regardless of the heat treatment temperature. The temperature gradient of the expanded ceramics which was heat treated at $650^{\circ}C\;was\;300^{\circ}C$. The bulk specific gravity, porosity, pore size, pore characteristics and wall thickness were varied depending on heat treatment temperature, and the compressive strength and the temperature gradient were governed by the complex effects of these factors.