조병욱(Byoung-Uk Cho),원종명(Jong Myoung Won) 한국펄프.종이工學會 2011 펄프.종이技術 Vol.43 No.5
Filler loading at thick stock was carried out in order to verify if the dual addition of filler can be used as a means to reduce the detrimental effects of filler on the strength properties of paper. PCC was added to 3.5% pulp slurry blended with HwBKP, BCTMP and SwBKP. Cationic starch was used as a fixing agent. The mixture of PCC and pulp was stirred for 5, 10 and 20min. at 1,000 rpm. The remaining PCC was washed out before handsheet making. PCC particles were flocculated and fixed on the pulp fiber and/or space between fibers. It is expected that the flocculation and inclusion of PCC can be helpful to improve the strength properties of paper due to the reduction of detrimental effect in fiber bonding. The distinct tendency in PCC flocculation and fixing on pulp fiber was not observed by the change of cationic starch dosage and treatment time.
PVAm 적용이 백상지의 형광증백제 발현효율에 미치는 영향
조병욱(Byoung-Uk Cho),원종명(Jong Myoung Won) 한국펄프·종이공학회 2016 펄프.종이技術 Vol.48 No.3
Effects of cationic polyvinylamine (PVAm) dry strength agent on effectiveness of optical brightening agent (OBA) during fine papermaking and the mechanism for brightness reduction of paper by PVAm was investigated by UV/Vis spectroscopy and turbidity measurement of OBA solution with PVAm. It was shown that PVAm reduced brightness of paper while opacity was not varied and tensile strength of paper was increased. Tetra-type OBA solution showed the peaks around the wavelength of 280 nm and 330 nm and the increase in the OBA concentration increased the UV absorbance in all wavelength. Addition of PVAm into the OBA solution decreased the UV absorbance at 280 nm. Turbidities of OBA and PVAm solutions were close to zero, respectively, while the turbidity value increased for the mixed solution of OBA and PVAm in various mixing ratios and the highest value was obtained when the mixing ratio of PVAm and OBA was 5:5, meaning that cationic PVAm formed complex with anionic OBA. In conclusion, cationic PVAm could form a complex with anionic OBA and that reduced UV absorbance, resulting in the reduced brightness of paper.