MgCO₃와 사문석을 사용한 마그네시아 시멘트의 특성평가

이종규,소정섭,추용식,송훈,박지선,Lee, Jong-Kyu,Soh, Jung-Sub,Chu, Yong-Sik,Song, Hun,Park, Ji-Sun 한국재료학회 2012 한국재료학회지 Vol.22 No.11

MgO based cement for the low-temperature calcination of magnesite required less energy and emitted less $CO_2$ than the manufacturing of Portland cements. Furthermore, adding reactive MgO to Portland-pozzolan cement can improve their performance and also increase their capacity to absorb atmospheric $CO_2$. In this study, the basic research for magnesia cement using $MgCO_3$ and magnesium silicate ore (serpentine) as starting materials was carried out. In order to increase the hydration activity, $MgCO_3$ and serpentinite were fired at a temperature higher than $600^{\circ}C$. In the case of $MgCO_3$ as starting material, hydration activity was highest at $700^{\circ}C$ firing temperature; this $MgCO_3$ was completely transformed to MgO after firing. After the hydration reaction with water, MgO was totally transformed to $Mg(OH)_2$ as hydration product. In the case of using only $MgCO_3$, compressive strength was 35 $kgf/cm^2$ after 28 days. The addition of silica fume and $Mg(OH)_2$ led to an enhancements of the compressive strength to 55 $kgf/cm^2$ and 50 $kgf/cm^2$, respectively. Serpentine led to an up to 20% increase in the compressive strength; however, addition of this material beyond 20% led to a decrease of the compressive strength. When we added $MgCl_2$, the compressive strength tends to increase.

잉어(Cyprinus carpio)로부터 분리된 Aeromonas hydrophila의 extracelluar proteases 연구

이종규,김종필,최태진,송영환,Lee, Jong-Kyu,Kim, Jong-Pil,Choi, Tae-Jin,Song, Young-Hwan 한국어병학회 1997 한국어병학회지 Vol.10 No.1

Aeromonas hydrophila isolated from the intestine of carp produced several kinds of proteases into the medium. Inhibitor assay with the culture supernatant of A. hydrophila showed that there were major metalloproteases and minor serine proteases. Gelatin SDS-PAGE showed two proteolytic bands. One broad protease band was inhibited by metalloprotease specific inhibitor, EDTA, indicating a metalloprotease. The other was inhibited by serine protease specific inhibitor, PMSF, suggesting a serine protease. The proteolytic activities of both extracellular proteases remained on Gelatin SDS-PAGE after heating at $70^{\circ}C$ for 30 min. However, the major metalloprotease was separated into two proteolytic bands on Gelatin PAGE by gel filtration chromatography on Sephadex G-75. 잉어로부터 분리한 Aeromonas hydrophila는 세포 밖으로 여러 종류의 proteases를 생산한다. A. hydrophila의 배양 상층액을 이용한 inhibitor assay를 통하여, 주된 활성을 나타내는 metallopretease와 약한 활성을 나타내는 serine protease가 있음을 알게 되었다. Gelatin SDS-PAGE를 통하여 두 개의 활성 band가 관찰되었으며, 이 들 중 넓게 퍼진 band는 metalloprotease에 특이하게 작용하는 inhibitor인 EDTA에 의해 활성이 상실되었고 따라서 metalloprotease임을 알 수 있었다. 다른 하나는 serine protease에 특이하게 반응하는 inhibitor인 PMSF에 의해 저해되어 serine protease임을 알 수 있었다. 이러한 두 extracellular protease의 활성은 $75^{\circ}C$에서 30 분간 열을 가한 후에도 Gelatin SDS-PAGE상에 남아있었다. 그런데, 주된 metalloprotease는 Sephadex G-75를 이용한 column chromatography를 거친 후 Gelatin Gel상에서 두 개의 band로 분리되었다.

저온 소결 유전체에 관한 연구

이종규,김왕섭,김경용,Lee, Jong-Kyu,Kim, Wang-Sup,Kim, Kyeong-Yong 한국재료학회 1992 한국재료학회지 Vol.2 No.4

본 실험에서는 낮은 음의 온도계수를 갖는 저온 소결 유전체에 대해 연구하였다. 새로 개발된 재료의 조성은 Ti$O_2$(100-X) CuOx(X=1~5wt%)에 미량의 Mn$O_2$를 첨가 하였다. CuO를 첨가하지 않은 경우에는 저온 (90$0^{\circ}C$) 에서 소결이 진행되지 않았다. CuO 함량이 증가할수록 저온에서 소결이 가능하였으나, 유전율이 낮아지고 유전손실은 증가 하였다. Mn$O_2$를 0.6wt% 첨가한 경우 유전율과 Q값이 가장 높게 나타났다. Low-firing dielectric materials with negative small temperature coefficients were investigated. The newly developed materials are based on Ti$O_2$(100-x)/ CuOx(X=1~5wt%) with small amount of Mn$O_2$ additive. The sample without CuO was not sintered at 90$0^{\circ}C$. As CuO content was increased the sample could be sintered at low temperature. However, the dielectric constant was decreased and the dielectric loss was increased. In the case of adding 3wt% CuO and 0.6wt% Mn$O_2$, the dielectric constant and the Q values appeared very high.

부분상태 궤환제어를 이용한 비선형 천정크레인의 진자각제어

이종규,이상룡,Lee, Jong-Kyu,Lee, Sang-Ryong 대한기계학회 1997 大韓機械學會論文集A Vol.21 No.6

The purpose of this study is to design an anti-sway motion for industrial overhead cranes which transport objects on a horizontal plane by adjusting movements of a trolley motor and a girder motor. The movement of a hoist motor has not been considered at this time since its role was assumed to move objects only vertically, therefore, not to affect the swing motion of objects. The dynamic behavior of the swing motion shows nonlinear characteristics, which makes the design of anti-sway motion controller difficult. First of all, the nonlinear state equation for the motion of industrial overhead cranes has been derived. Then they have been linearized about normal operating states determined by the dynamic characteristics of motor motion-acceleration, constant speed, and deceleration, and deceleration, during transportation. The partial state feedback control algorithm based on this linearized state equation has been developed on order to suppress the swing motion. The simulation results have demonstrated satisfactory performance of the proposed controller.

석고계 바인더를 활용한 습도도절 세라믹 보드의 특성 평가

이종규,김태연,Lee, Jong-Kyu,Kim, Tae-Yeon 한국재료학회 2018 한국재료학회지 Vol.28 No.1

Active clay, bentonite and zeolite were used as porous materials for humidity controlling ceramic boards. The specific area and the pore volume of active clay were higher than bentonite and zeolite. The flexible strength of the gypsum board decreased with an increasing amount of porous material, and the flexible strength was lowest when active clay with a higher specific surface area than others porous materials was added. The specific surface area and total pore volume of ceramic boards containing porous material were highest at $102.25m^2/g$, $0.142cm^3/g$, respectively, when the active clay was added. In addition, as the amount of added porous materials increased, the specific surface area and total pore volume of the ceramic board increased, but the average pore diameter decreased. The addition of s porous materials with a high specific area and a large pore volume improved the moisture absorptive and desorptive performance of the ceramic board. Therefore, in this experiment, the moisture absorptive and desorptive properties were the best when active clay was added. Furthermore, as the amount of added porous materials increased, the moisture absorptive and desorptive properties improved. When 70 mass% of active clay was added to ${\alpha}$-type gypsum, the hygroscopicity was the highest, about $300g/m^2$, in this experiment.

영지의 새로운 병원성진균 Xylogone sphaerospora

이종규,최경자,조광연,오세종,박정식 ( Jong Kyu Lee,Gyung Ja Choi,Kwang Yun Cho,Se Jong Oh,Jeong Sik Park ) 한국균학회 1996 韓國菌學會誌 Vol.24 No.4

클링커 제조 조건에 따른 수용성 6가 크롬 용출 특성

이종규,추용식,송훈,Lee, Jong-Kyu,Chu, Yong-Sik,Song, Hun 한국재료학회 2011 한국재료학회지 Vol.21 No.12

One of the trace constituents included in cement clinker, chromium, has become prominent and highly noticed lately as a social issue both inside and outside of this country because it affects the human body negatively. The purpose of the present study was to investigate leaching properties of water-soluble hexavalent chromium by different manufacturing conditions of cement clinker. Raw materials were prepared to add different $SiO_2$, $Al_2O_3$ and $Fe_2O_3$ sources. After the raw materials, such as limestone, sand and clay, iron ore was pulverized and mixed, and the raw meal was burnt at $1450^{\circ}C$ in a furnace with an oxidizing atmosphere. Leaching of soluble hexavalent chromium showed a tendency to decrease with an increasing LSF and IM. However, leaching of soluble hexavalent chromium increased with an increasing S.M. Alkali contents of iron source minerals is closely related to the leaching properties of soluble hexavalent chromium. Green sludge has the highest content of alkali added; leaching of water-soluble hexavalent chromium was mostly high. In order to reduce the water-soluble hexavalent chromium in cement, reducing the alkali content in raw materials is important.

MgCO₃와 사문석을 사용한 마그네시아 시멘트의 무기 첨가제 영향

이종규,소정섭,Lee, Jong-Kyu,Soh, Jung-Sub 한국재료학회 2015 한국재료학회지 Vol.25 No.2

The carbon dioxide($CO_2$) released while producing building materials is substantial and has been targeted as a leading contributor to global climate change. One of the most typical method to reducing $CO_2$ for building materials is the addition of slag and fly ash, like pozzolan material, while another method is reducing $CO_2$ production by carbon negative cement development. The MgO-based cement was from the low-temperature calcination of magnesite required less energy and emitted less $CO_2$ than the manufacturing of Portland cements. It is also believed that adding reactive MgO to Portland-pozzolan cements could improve their performance and also increase their capacity to absorb atmospheric $CO_2$. In this study, the basic research for magnesia cement using $MgCO_3$ and magnesium silicate ore (serpentine) as main starting materials, as well as silica fume, fly ash and blast furnace slag for the mineral admixture, were carried out for industrial waste material recycling. In order to increase the hydration activity, $MgCl_2$ was also added. To improve hydration activity, $MgCO_3$ and serpentinite were fired at $700^{\circ}C$ and autoclave treatment was conducted. In the case of $MgCO_3$ as starting material, hydration activity was the highest at firing temperature of $700^{\circ}C$. This $MgCO_3$ was completely transferred to MgO after firing. This occurred after the hydration reaction with water MgO was transferred completely to $Mg(OH)_2$ as a hydration product. In the case of using only $MgCO_3$, the compressive strength was 3.5MPa at 28 days. The addition of silica fume enhanced compressive strength to 5.5 MPa. In the composition of $MgCO_3$-serpentine, the addition of pozzolanic materials such as silica fume increased the compression strength. In particular, the addition of $MgCl_2$ compressive strength was increased to 80 MPa.

천장크레인의 무인운전 시스템을 위한 운동제어 알고리즘 개발

이종규,박영조,이상룡,Lee, Jong-Kyu,Park, Young-Jo,Lee, Sang-Ryong 대한기계학회 1996 大韓機械學會論文集A Vol.20 No.10

A search algorithm for the collision free, time optimal transport path of overhead cranes has been proposed in this paper. The map for the working environment of overhead cranes was constructed in the form of three dimensional grid. The obstacle occupied region and unoccupied region of the map has been represented using the octree model. The best-first search method with a suitable estimation function was applied to select the knot points on the collision free transport path to the octree model. The optimization technique, minimizing the travel time required for transporting objects to the goal while subjected to the dynamic constraints of the crane system, was developed to find the smooth time optimal path in the form of cubic spline functions which interpolate the selected knot points. Several simulation results showed that the selected estimation function worked effectively insearching the knot points on the collision free transport path and that the resulting transport path was time optimal path while satisfying the dynamic constraints of the crane system.