$TiO_2$ 첨가에 따른 붕규산 유리의 분상에 관한 연구
박용완,민병욱 한국세라믹학회 1981 한국세라믹학회지 Vol.18 No.4
The tendency of glass containing titanium-dioxide to separate into two phases can be attributed to a change of the coordination number of titanium from six to four on increase of temperature and to "freezing" of the high temperature four fold coordination on cooling of the melt. Addition of TiO2 to the basic glass 8.7 $Na_2O$ 22.4B2O3 68.9 $SiO_2$ was varied 5 to 25 parts. The phase separation in the temperature range of transformation was examined with each heating temperature and soaking time. As the experimental results, the most distinct phase separation were obtained from alkali extraction method when $TiO_2$ was added 15 parts. The apparant activation energy was 30.5 Kcal/mole by alkali extraction method derived from Arrhenius plots.ius plots.
박용완,강은태,박찬성,전문덕 한국세라믹학회 1980 한국세라믹학회지 Vol.17 No.4
A glass-ceramics material of composition %SiO_2$: 38.50, $Al_2O_3$: 26.00, $Na_2O$: 18.00, CaO: 6.00, MgO: 4.00, $TiO_2$: 7.50 was strengthened by coating a series of glazes$(SiO_2-B_2O_3-Al_2O_3-CaO-PbO-Na_2O-)$, which has lower thermal expansion coefficient than that of the glass-ceramics. The thermal expansion coefficient of the glazes ranges $80~90{\times}10^{-7}$cm/cm/$^{\circ}C$, whereas that of the glass-ceramics is $115{\times}10^{-7}$cm/cm/$^{\circ}C$. The glass-ceramics was identified to be composed of nepheline, carnegieite low form, and meta sodium silicate crystal by X-ray diffraction phase analysis. The glaze, having lower melting point and appropriate thermal expansion coefficient, was tried to be stable and good at secondary heat treatment.
ZnO-P$_2$O$_5$ 계 유리의 결정화 기구에 관한 연구
박용완,연석주 한국세라믹학회 1991 한국세라믹학회지 Vol.28 No.9
ZnO-P2O5 system glass containing 45 to 60 mol% ZnO has been melted at 120$0^{\circ}C$ and crystallized through heat treatment. Each condition of crystallization was determined by measurement of dilatometric softening point and DTA. The principal crystalline phase was identified as zinc metaphosphate [Zn(PO3)2] in the glasses containing 45~55 mol% ZnO and zinc pyrophosphate (Zn2P2O7) in the sample of 60 mol% ZnO with X-ray diffraction patterns. The crystalline mechanism was investigated by XRD and SEM. As the results, the specimens containing 50~60% ZnO showed the existence of oriented structure due to one-dimensional crystal growth.
박용완,허수정 에스케이텔레콤 (주) 2014 Telecommunications Review Vol.24 No.2
디지털기술의 진전과 소비자 수요 변화 등의 패러다임 전환은 통신서비스 흐름을 전체적으로 변화시키고 있으며 4세대 기반의 스마트폰 중심의 통신서비스는 산업의 경제적 성장까지 주도하여 소비자의 삶과 생활 패턴에도 영항을 미치고 있다. 그러나 급변하는 사회현상과 고도화되어가는 산업 환경, 다양화 개인화되는 소비자의 요구를 충족시킬 수있는 차세대 이동통신서비스의 필요성이 대두되면서 5세대(5G)를 준비하고 있다. 4G 이동통신서비스의 한계, 새로운 멀티미디어 통신기기의 보급, 사물인터넷의 확장에 대한 5G 환경으로의 변화 필요를 통해 5G 서비스에서는Quadruple 1000을 제시하고 이를 지원하기 위한 5가지 서비스기술을 제시한다. 5G 서비스를 지원하기 위한 서비스기술 목표로 초반응성, 초연결성, 초실감형, 초저가형, 초절전형, 초신뢰성을 명명하고 차세대 5G 서비스 비전과 그에따른 핵심 응용서비스를 소개한다. 4G의 서비스 한계를 넘을 수 있는 5G의 서비스 도출은 서비스주도형 산업구조에서 반드시 필요한 연구 분야이며 도출된 서비스를 지원할 수 있는 기술의 개발로 전 세계 5G를 주도해 나갈 수 있을것으로 기대한다.