http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
인프라 구조물 안전관리 분야의 클라우드 기반 빅데이터 해외 사례와 국내 적용성 고찰
이강문 ( Lee Kang Moon ),남동우 ( Nam Dong Woo ),이정훈 ( Rhee Jeong Hoon ),문대중 ( Moon Dae Jung ) 한국구조물진단유지관리공학회 2017 한국구조물진단유지관리공학회 학술발표대회 논문집 Vol.21 No.2
Many of the structures constructed since the 1970s have begun to deteriorate. As a result, safety inspection / diagnosis and maintenance are expected to increase further, and long-term and systematic measures are urgently needed to prepare for the aging of major infrastructures. Currently, the safety inspection and maintenance of the structure is carried out by the method based on the utilization of the measurement data and the manager's experience, but the reliability and the accuracy are still insufficient. In other words, there is a limit to understanding the state change of bridges, such as abnormal behavior and gradual damages, therefore, it is necessary to have an accurate and reliable monitoring process using new techniques and systems. For this reason, I would like to examine the possibility of using cloud and big data in the field of infrastructure safety management.
재생(再生)잔골재(骨材)를 프리캐스트 콘크리트용(用) 골재(骨材)로 활용(活用)하기 위한 실험적(實驗的) 연구(硏究)
문대중,문한영,김양배,임남웅,Moon, Dae-Joong,Moon, Han-Young,Kim, Yang-Bae,Lim, Nam-Woong 한국자원리싸이클링학회 2006 資源 리싸이클링 Vol.15 No.2
폐콘크리트 파쇄시 발생하는 재생잔골재의 품질을 검토하였으며, 재생잔골재를 활용한 모르타르의 압축강도, 휨강도 및 흡수율을 검토하였다. 또한, 프리캐스트 콘크리트 제품용 골재로서의 적용성에 대하여 평가하였다. 재생잔골재의 밀도 및 흡수율은 각각 $2.31\;g/cm^3$ 및 8.07%로 KS F 2573의 2종에 해당되는 품질이었다. 혼합시멘트 MRS1, MRS2 및 MRS3 사용 모르타르의 재령 28일 압축강도는 물-시멘트비 35%, 양생온도 $40^{\circ}C$의 조건에서 각각 15.8, 27.4 및 48.7MPa로 최대값을 발현하였다. 모르타르의 최대휨강도는 혼합시멘트 MRS1 및 MRS2 사용시 물-시멘트비 35.0%, 양생온도 $40^{\circ}C$, 혼합시멘트 MRS3사용시 물-시멘트비 37.5%, 양생온도 $40^{\circ}C$의 조건에서 발현하였다. 혼합시멘트 MRS1, MRS2 및 MRS3를 사용한 모르타르의 흡수율의 범위는 각각 $8.3{\sim}7.3%,\;6.5{\sim}8.5%$ 및 $3.5{\sim}6%$의 범위로 나타났다. 그러므로 혼합시멘트와 재생잔골재의 비율을 적절히 조절함으로써 MRS1는 저강도용, MRS2는 보통강도용, MRS3는 고강도용으로 다양한 프리캐스트 콘크리트 제품에 적용될 수 있을 것으로 기대된다. The duality of recycled fine aggregate (RS) which was produced at the waste concrete crushing was investigated. The compressive strength, flexural strength and absorption of mortar utilized with RS were examined. It was evaluated on the application of RS as precast concrete aggregate. The density and absorption of RS were $2.31g/cm^3$ and 8.07% respectively, the quality of RS was satisfied with the criterion of KS F 2573 type 2. The maximum 28days compressive strength of mortar mixed with blended cement MRS1, MRS2 and MRS3 were developed with 15.8, 27.4 and 48.7MPa respectively, in condition to curing temperature $40^{\circ}C$ and water-cement ratio 37.5%. When blended cement MRS1 and MRS2 were used, the maximum flexural strength of mortar was developed at curing temperature $40^{\circ}C$ and water-cement ratio 35.0%. When blended cement MRS3 was used, the maximum flexural strength of mortar was developed at curing temperature $40^{\circ}C$ and water-cement ratio 37.5%. The absorption of mortar mixed with blended cement MRS1, MRS2 and MRS3 were indicated the range of $8.3{\sim}7.3%,\;6.5{\sim}8.5%$ and $3.5{\sim}6%$ respectively. Therefore, when the ratio of blended cement and RS is appropriately centre]led, it would be expected that MRS1, MRS2 and MRS3 will be able to apply the variable low strength, medium strength and high strength precaste concrete.