김성훈,김경훈,도환수,박주석,김경자,심광보,Kim, Seong-Hoon,Kim, Kyung-Hun,Dow, Hwan-Soo,Park, Joo-Seok,Kim, Kyung-Ja,Shim, Kwang-Bo 한국결정성장학회 2016 韓國結晶成長學會誌 Vol.26 No.2
본 연구에서는 열간가압소결법으로 SiC를 소결하여 균열자기치유 특성을 분석하였다. SiC는 $Al_2O_3$와 $Y_2O_3$를 소결조제로 $1950^{\circ}C$, 50 MPa, 아르곤(Ar) 분위기에서 소결하였다. 소결된 시편을 $3{\times}4{\times}40mm$, 절단 및 가공하고, Vickers 경도기를 이용하여 49.6 N으로 예비균열을 생성하였다. $1200{\sim}1400^{\circ}C$, 1~10시간 산화분위기에서 열처리한 후 XRD, SEM, 3점 굽힘강도를 측정하였다. $1300^{\circ}C$ 1시간에서 741 MPa, 5시간에서 770 MPa로 가장 우수한 균열자기치유 효과를 나타내는 것으로 분석되었다. In this study, it was investigated that characteristic of crack-self-healing of hot-pressed SiC. SiC ceramics was sintered with $Al_2O_3$ and $Y_2O_3$ sintering additive by hot press. Sintering was performed in hot-press furnace in flowing argon (Ar), holding for 3 hr under $1950^{\circ}C$ and 50 MPa. The sintered SiC was machined into 3-point bending strength specimen of $3{\times}4{\times}40mm$, and introduced pre-crack by Vickers indentation at 49.6 N. Specimens were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), 3-point bending strength after heat treatment at $1200{\sim}1400^{\circ}C$ for 1~10 hr. The best crack-self-healing ability was achieved 770 MPa 3-point bending strength by heat treatment at $1300^{\circ}C$ for 5 hr.
상압소결 질화알루미늄의 소결 첨가제 변화에 따른 열적 및 기계적 특성
황진욱,문소윤,남상용,도환수,Hwang, Jin Uk,Mun, So Youn,Nam, Sang Yong,Dow, Hwan Soo 한국분말야금학회 2019 한국분말재료학회지 (KPMI) Vol.26 No.5
Aluminum nitride (AlN) has excellent electrical insulation property, high thermal conductivity, and a low thermal expansion coefficient; therefore, it is widely used as a heat sink, heat-conductive filler, and heat dissipation substrate. However, it is well known that the AlN-based materials have disadvantages such as low sinterability and poor mechanical properties. In this study, the effects of addition of various amounts (1-6 wt.%) of sintering additives $Y_2O_3$ and $Sm_2O_3$ on the thermal and mechanical properties of AlN samples pressureless sintered at $1850^{\circ}C$ in an $N_2$ atmosphere for a holding time of 2 h are examined. All AlN samples exhibit relative densities of more than 97%. It showed that the higher thermal conductivity as the $Y_2O_3$ content increased than the $Sm_2O_3$ additive, whereas all AlN samples exhibited higher mechanical properties as $Sm_2O_3$ content increased. The formation of secondary phases by reaction of $Y_2O_3$, $Sm_2O_3$ with oxygen from AlN lattice influenced the thermal and mechanical properties of AlN samples due to the reaction of the oxygen contents in AlN lattice.