Sintering behavior, distribution of dopant oxides and electrical properties in the ZnO-Bi2O3-CoO-Sb2O3 and ZnO-Bi2O3-CoO-Sb2O3-Cr2O3 systems were studied. The linear shrinkage of ZnO varistors from 850 to 950$^{\circ}C$ was related to the decomposition reaction (py\longrightarrowsp+Bi2O3) of the pyrochlore phase. In the distribution of the dopant oxides (CoO, Sb2O3, Cr2O3), Co distribute uniformly throughout the sample, the distribution of Sb coincided with small particles (spinel phase, Zn7Sb2O12), and Cr distributed very consistently with Sb. The increase in breakdown voltage, due to the addition of Cr2O3, was not only attributed to the decrease in the ZnO grain size but also to the solution of Cr2O3 in the spinel phase. The leakage current (80% V60 ${\mu}\textrm{A}$) was increased by the addition of Cr2O3.
$\alpha-Zn_7Sb_2O_{12}$ 첨가에 의한 Zinc Oxide 바리스터의 전기적 특성
김경남,한상목 한국세라믹학회 1994 한국세라믹학회지 Vol.31 No.11
Electrical properties in the ZnO-Bi2O3-CoO-Zn7Sb2O12 system were investigated with Zn7Sb2O12 content (0.1~2 mol%). The increase of the Zn7Sb2O12 content inhibited the grain growth of ZnO, which showed a narrow grain size distribution of ZnO. The breakdown voltage (Vb) increased markedly with 1 mol% Zn7Sb2O12 addition due to the grain growth control behaviour of the Zn7Sb2O12 . The nonlinear I-V characteristic was significantly influenced by the Zn7Sb2O12 content (or Bi2O3/Zn7Sb2O12 ratio). Addition of 0.5 mol% Zn7Sb2O12 showed the highest nonlinear coefficient ($\alpha$) of 43. The leakage current in prebreakdown region was decreased with increasing Zn7Sb2O12 content.
$Zn_7Sb_2O_{12}$ 첨가량이 ZnO 바리스터의 입자성장과 미세구조에 미치는 영향
김경남,한상목 한국세라믹학회 1993 한국세라믹학회지 Vol.30 No.11
Sintering behavior and microstructure development in the system ZnO-Bi2O3-CoO-Zn7Sb2O12 with Zn7Sb2O12 content(0.1mol%~2mol%) were studied. The pyrochlore phase was formed by the reaction of the Zn7Sb2O12 with Bi2O3 phase during heating (below 90$0^{\circ}C$). The formation temperature of the liquid phase (Bi2O3) was dependent on the Zn7Sb2O12 contents (about 74$0^{\circ}C$ for Bi2O3/Zn7Sb2O12>1 by the eutectic melting in the ZnOBi2O3 system, and about 110$0^{\circ}C$ for Bi2O3/Zn7Sb2O12 1 by the decomposition of pyrochlore phase). Hence, sintering behavior and microstructure development were determined virtually by the Bi2O3/Zn7Sb2O12 ratio, which were promoted by liquid (Bi2O3) phase and retarded by the pyrochlore (or spinel) phase. The grain growth of ZnO during sintering was sluggish with increasing Zn7Sb2O12 contents.