논문 : 초음파 나노표면개질 공정기술에 의한 AISI304 스테인리스강의 표면나노구조화 및 압축잔류응력 형성
조인식 ( In Shik Cho ),동계령 ( Ji Ling Dong ),유대황 ( Dae Hwang Yoo ),서정화 ( Jung Hwa Suh ),아마노프 ( Auezhan Amanov ),신기삼 ( Kee Sam Shin ),이창순 ( Chang Soon Lee ),편영식 ( Young Shik Pyoun ),박인규 ( In Gyu Park ) 대한금속재료학회 ( 구 대한금속학회 ) 2010 대한금속·재료학회지 Vol.48 No.9
In this paper, the Ultrasonic Nanocrystalline Surface Modification (UNSM) surface treatment process was used to induce compressive residual stress and nanocrystalline structure by severe plastic deformation on the UNSM-treated surface. The test results for AISI304 stainless steel demonstrated that the grain size was found to be 23 nm, the dislocation density was increased by 0.2085×10(18) m-2, and the volume fraction of martensite is defined as 27.6% from austenite so that the surface hardness of the surface is increased from 200 Hv up to 515 Hv. The initial tensile residual stress is changed from 300 MPa to a compressive residual stress of 500 MPa after UNSM treatment. In addition, UNSM was applied under five various conditions, and the results of those conditions were defined as a function of depth quantitative.
Ti-6Al-4V 재의 UNSM 처리에 의한 피로특성변화
서민수(Min-Soo Suh),편영식(Young-Shik Pyoun),서창민(Chang-Min Suh) 대한기계학회 2012 大韓機械學會論文集A Vol.36 No.4
Ti-6Al-4V 재에 다양한 표면처리방법을 통하여 나노스킨화된 피로시험편을 제작하고 회전굽힘피로 시험과 축하중 인장압축피로시험을 수행하였다. 특히 S-N 곡선에서 초음파나노표면개질(UNSM)법은 국내특허기술로 다른 처리법들보다 우수한 결과를 보였고, UNSM 처리된 직경 5 ㎜ 재는 6 ㎜ 티타늄재를 대치 가능할 성능을 얻었다. UNSM 처리된 10? 사이클 이상의 장수명영역에서 피로강도가 크게 향상되는 시험결과를 얻었다. 균열발생 패턴의 분석을 통하여 Ti-6Al-4V 재는 응력의 작용형태에 따라 표면균열발생형(surface originating crack type)과 내부균열발생형(interior originating crack type)인 어안균열(fish eye crack)이 발생하는 메커니즘을 분석하였다. Nanoskins were fabricated on a Ti-6Al-4V material by carrying out various surface treatments, i.e., deep rolling, laser shot peening, and ultrasonic nanocrystal surface modification (UNSM). These surface treatments are newly developed techniques and are becoming more popular for industrial applications. Fatigue tests were carried out using material test system (MTS); these tests included the axial loading tension-compression fatigue test (R = ?1, RT, 5 ㎐, sinusoidal wave) and rotating bending fatigue test (R = ?1, RT, 3200 rpm). The analysis of the crack initiation pattern in the UNSM-treated material indicated that the crack was interior originating in the axial loading tension-compression cycle, and was surface originating in the bending fatigue test. UNSM treatment significantly improved the fatigue strength for the regime of above 10? cycles that S-N curve of rotating bending stress clearly show the performance of a 5 ㎜ titanium specimen after UNSM treatment is similar to that of an untreated 6 ㎜ titanium specimen.
나이티놀 스텐트 와이어의 기계적 특성 향상을 위한 초음파 나노표면 개질 처리에 대한 연구
김상호,서태석,이창순,박인규,조인식,편영식,김성현,Kim, Sang-Ho,Suh, Tae-Suk,Lee, Chang-Soon,Park, In-Gyu,Cho, In-Sik,Pyoun, Young-Shik,Kim, Seong-Hyeon 한국의학물리학회 2009 의학물리 Vol.20 No.2
Phase transformation, superelastic characteristics and variation of surface residual stress were studied for Nitinol shape memory alloy through application of UNSM technology, and life extension methods of stent were also studied by using elastic resilience and corrosion resistance. Nitinol wire of ${\phi}1.778$ mm showed similar surface roughness before and after UNSM treatment, but drawing traces and micro defects were all removed by UNSM treatment. It also changed the surface residual stress from tensile to compressive values, and XRD result showed less intensive austenite peak and clear martensite and additional R-phase peaks after UNSM treatment. Fatigue resistance could be greatly improved through removal of surface defects and rearrangement of surface residual stress from tensile to compressive state, and development of surface modification system to improve not only bio-compatability but also resistance to corrosion and wear will make it possible to develop vascular stent which can be used for circulating system diseases which run first cause of death of recent Koreans. 비혈관 스텐트(식도용, 담도용, 대장용, 십이지장용, 기관지용) 재질로 가장 널리 사용되고 있는 Nitinol wire 형상기억합금의 기계적 특성 향상을 위해 초음파 나노표면 개질(UNSM) 기술을 적용하여 Nitinol wire의 상변화와 초탄성 특성 및 표면 잔류응력 등의 변화를 연구하였으며, 탄력에너지와 부식내구성을 통한 스텐트의 수명 연장방법을 연구하고자 하였다. 본 연구에 사용된 Nitinol wire는 ${\phi}1.778$ mm로 UNSM 처리 전후의 표면거칠기 값은 Ra=0.092${\mu}m$와 Ra=0.093${\mu}m$로 비슷 하였지만, 초기시편에서는 미세결함과 인발가공 흔적이 확연히 관찰되었으나, UNSM 후에는 인발가공 흔적과 미세 표면 결함은 사라진 것이 발견되었다. 또한 잔류응력 측정 결과, 초기 시험편에는 +3.65 MPa였으나 UNSM 처리 후에는 -4.09 MPa로 확인되었으며, XRD를 통한 결정구조 분석 결과 $42.28^{\circ}$에서 초기보다 약한 (110) 오스테나이트 피크가 관찰되었으며, 대신 (020), ($1{\overline{1}}1$), 그리고 (021) 피크가 명확히 Martensite (B19' Monoclinic lattices) 구조로 확인되었고, (300)의 R상 (Rhombohedral lattices)에 대한 추가 피크가 미비하게 관찰되었다. 탄성변형에 따른 에너지 흡수력과 하중 제거에 따른 에너지의 회복력인 탄력계수(modulus of resilience) $U_r$은 단위체적당 변형률 에너지로 4.31 $MJ/m^3$에서 5.85 $MJ/m^3$로 증가하였다. 이와 같이 표면결함 제거와 인장응력을 압축응력으로 재편성하는 것만으로도 피로내구성을 크게 향상시킬 수 있다고 사료되며, 생체적합성과 더불어 내부식성, 내마모성 및 내구수명 향상을 실용화할 수 있는 표면개질 장치가 개발된다면, 현재 한국인 사망원인 1위인 순환계 질환(심근경색, 뇌졸중 등)에 사용되는 혈관계통의 스텐트 개발에도 응용개발연구가 가능할 것으로 예상된다.
A quality control method by ultrasonic vibration energy and diagnosis system at trimming process
Ju-Ho Jang(장주호),Chang-Min Suh(서창민),Gil-Ho Song(송길호),Young-Shik Pyoun(편영식) 대한기계학회 2006 대한기계학회 춘추학술대회 Vol.2006 No.11
In this paper, the mechanical characteristics of ultrasonic cold forged technology (UCFT) used for the trimming knife and the effects of ultrasonic vibration energy (UVE) into the trimming process on the state of the strip cutting face were studied. A diagnosis system to quality control for trimming knife and strip cutting face was developed and installed in plant. By the plant application of UCFT, service life of knife was more increased over 100% than that of conventional knife. And using the developed diagnosis system, the knife breakage and saw ear have been perfectly detected and quality control of trimming face is obtained effectively.