Poly ( phenylene sulfide sulfone ) 의 경화에 관한 연구
서관호,박이순,오대희 ( Kwan Ho Seo,Lee Soon Park,Dae Hee Oh ) 한국공업화학회 1993 공업화학 Vol.4 No.3
Poly(phenylene sulfide sulfone)[PPSS]를 시간과 온도를 변화시키면서 열처리를 하였을 때 이들의 유리전이 온도(T_g)를 DSC로서 조사하였다. 그 결과 PPSS의 T_g는 열처리온도가 230℃까지는 열처리 시간이 길어질수록 증가하다가 평형에 도달하였다. 열처리 온도가 245℃ 이상에서는 열처리 시간이 길어질수록 T_g가 증가하다가 어느 정도 시간이 되면 감소한 뒤 다시 증가하는 것으로 나타났다. 이 현상을 경화가 진행됨에 따른 chain extension반응과 oxidative crosslinking 및 thermal crosslinking으로 설명하였다. Glass transition temperatures(T_g) of poly(phenylene sulfide sulfone)[PPSS], which were heat treated at various temperature and time, were studied by DSC. UP to 230℃, T_g of heat treated PPSS were increased with increasing the heat treated time. When the sample was heated at 260℃ for 30 minute and 280℃ for 10 minute, however, T_g of those samples were decreased. These phenomena can be explained by the factors of chain extension reaction, oxidative crosslinking, and thermal crosslinking.
온달동굴 지형지물에 대한 관람 포인트 설정 및 관람루트에 관한 수치분석
서관호 ( Kwan Ho Seo ),신동원 ( Dong Won Shin ),조용호 ( Yong Ho Jo ) 한국동굴학회 2009 동굴 Vol.92 No.-
온달동굴 내에 분포하는 관람대상 지형지물과 관람객의 이동통로에 설정 가능한 관람 포인트를 구축하고 이에 따른 네트워크구축사례와 네트워크의 특성 분석을 통한 온달굴의 관람포인트의 특성을 고찰하였다. 온달동굴의 관람루트는 정해진 루트를 이동하기 때문에 그래프상의 목(tree)형 형태를 갖는다. 관람포인트와 관람대상물의 관계를 통한 관람루트의 특성을 네트워크 분석기법을 이용하여 분석하였다. 온달동굴의 수치적 결과는 차후 유사한 동굴간의 관람루트를 비교 분석하거나 관람방식에서 생기는 문제점을 파악하는 기초자료로 제공 될 수 있다. Due to the designated tour route of Ondal cave, it has a specific shape of a tree. The numerical results of Ondal cave`s tour route would be suggested as basic data for a comparative analysis between similar caves or a problem identified within the viewing route.
서관호 ( Kwan Ho Seo ),김대진 ( Dae Jin Kim ),민철희 ( Chul Hee Min ),박해윤 ( Hae Youn Park ),김상구 ( Sang Gu Kim ) 한국공업화학회 2013 공업화학 Vol.24 No.1
Poymer blends of two degradable aliphatic polyesters, relatively expensive material polylactic acid (PLA) and relatively inexpensive material poly(butylene adipate-co-terephthalate) (PBAT), were used in this study. Three different kinds of modifiers were used with various amounts. Diisocyanate type methylenediphenyl 4,4`-diisocyanate (MDI) and hexamethylene diisocyanate (HDI) were used as modifiers and epoxy type coupling agents also used. The melt flow index (MFI) and dynamic viscoelasticity of various compositions of PLA/PBAT blends were studied. The mechanical property and morphology with respect to the fracture surface of PLA/PBAT blends were also investigated using tensile test and field emission scanning electronic microscopy, respectively. These tests were also used to verify the compatibility of PLA/PBAT and the effect of mechanical properties due to the use of modifiers. Tensile properties of PLA/PBAT blends modified with HDI were improved remarkably.
리튬 이온 전지용 개스킷 고무 물성에 미치는 가교조제의 영향
서관호 ( Kwan Ho Seo ),강동국 ( Dong Gug Kang ),김혜영 ( Hye Young Kim ),강영임 ( Young Im Kang ),허병기 ( Byung Ki Hur ) 한국공업화학회 2011 공업화학 Vol.22 No.4
리튬 이온 전지에 사용되는 개스킷 재료는 내전해액성, 전기 절연성, 압축 영구 줄음률, 비오염성, 저온성이 요구된다. 개스킷 고무에 적용되는 가교조제의 영향을 살펴보기 위하여 리튬 이온 전지에 있어 대표적 용매인 propylene carbonate에서 용해도 지수의 차가 큰 ethylene propylene diene monomer (EPDM)에 금속산화물인 가교조제의 함량을 조정하여 compound를 배합하였다. 이렇게 배합된 compound를 리튬 이온 전지의 작동환경을 고려하여 전해액에 대한 장기평가 및 압축 영구 줄음률, 저온성에 대한 평가를 실시하였다. 본 실험에서는 다양한 가교조제를 사용하여 가교조제에 따른 고무재료의 물리적 화학적 특성 및 리튬 이온 전지에의 영향에 대하여 검토하였다. 가교조제로 ZnO를 사용한 고무에서 1000 h까지의 공기 노화 시험 및 전해액의 대표 유기용매인 propylene carbonate 침적시험에 대해 안정적인 물성을 얻 을 수 있었으나, 이온 용출성 평가에서는 Zn 2+가 용출되기 때문에 리튬 이온 전지용 개스킷에 적용되는 고무 배합에서 는 ZnO 사용을 제한하여야 한다. Material of the gasket for lithium ion battery requires the chemical resistance, the electrical insulting property, the compression set, the anti-contamination level and the low temperature resistance. We compounded ethylene propylene diene monomer (EPDM), which showed widely different solubility parameter index, with adjusting the amount of metal oxide as an activator. We did long-term test and compression set against an electrolyte with consideration for operating conditions in lithium-ion battery. In these tests, we checked the physical, chemical characteristics and the effect to lithium ion battery with different kinds of activators. In case of rubber with ZnO as an activator, through 1000 h depositing test in propylene carbonate which is one of representative solvents, we could get the satisfying characteristics and result. However, Zn 2+ had eluted in the ion elution test. So, ZnO should be limited in EPDM compound for the gasket material in lithium-ion battery.
아크릴계 4 원공중합체와 염화비닐 - 비닐프로피오네이트 공중합체와의 블렌드 점착물성
서관호(Kwan Ho Seo),오대희(Dae Hee Oh) 한국고무학회 1999 엘라스토머 및 콤포지트 Vol.34 No.4
N/A In this study, the blends of acrylic quaternary polymer (PEBEV) which was copolymerized from 2-ethylhexyl acrylate (2-EHA), n-butyl acrylate (BA) and ethyl acrylate (EA), vinyl acetate (VAc), and polyvinyl chloride-co-vinyl propionate) (PVCVP) were prepared by solution blending. Pressure sensitive adhesive (PSA) properties of PEBEV/PVCVP blends were compared with those of FEBEV/poly(vinyl chloride-co-vinyl acetate) (PVCVAc) blends. Compatibility of PEBEV/PVCVP was better than that of PEBEV/PVCVAc. Tackiness of both blend systems were similar, but holding power began to decrease at 15wt% or higher PVCVAc contents in PEBEV/PVCVAc blends. On the other hands, holding power of PEBEV/PVCVP increased as the contents of PVCVP increased. Failure modes of the blends were adhesive failure except 5wt% of PVCVP was blended.
리튬이온 전지용 가스켓 고무의 특성에 미치는 충전제의 영향
서관호(Kwan Ho Seo),조광수(Kwang Soo Cho),윤인섭(In Sub Yun),최우혁(Woo Hyuk Choi),허병기(Byung Ki Hur),강동국(Dong Gug Kang) 한국고분자학회 2010 폴리머 Vol.34 No.5
리튬이온 전지에 사용되는 가스켓 재료는 내전해액성, 전기절연성, 압축 영구 줄음률, 비오염성, 저온성이 요구된다. 가스켓 고무에 적용되는 충전제의 특성을 살펴보기 위하여 EPDM(ethylene propylene diene monomer), NBR(nitrile butadiene), FKM(fluoro elastomers)에 카본블랙 및 실라카계 충전제의 함량을 조정하여 compound를 만들었다. 이렇게 배합된 compound를 리튬이온 전지의 작동 환경을 고려하여 전해액에 대한 장기평가 및 압축 영구 줄음률, 저온성에 대한 평가를 실시하였다. 본 실험에서는 카본블랙 및 실리카계 충전제를 사용하여 각 충전제에 따른 고무재료의 물리적 화학적 특성에 대하여 검토하였다. The gasket materials of for the lithium ion battery requires chemical resistance to electrolyte, electrical insulating, compression set, anti-contamination and low temperature property. To check the special characteristics of fillers which are applied to rubber for gasket, compound of EPDM. NBR and FKM (fluoro elastomer) were made by adjusting weights of carbon black and silica additive. Using these compounds, we had done tests of long-term stability against electrolyte, compression set and low-temperature property with considering operating condition of the lithium ion battery. From this test, we investigated the physical and chemical characteristics of rubber with using of carbon black and silica additive in each.
리튬 이온 전지 씰링에의 응용을 위한 EPDM, NBR, FKM, VMQ 및 FVMQ 특성연구
서관호 ( Kwan Ho Seo ),조광수 ( Kwang Soo Cho ),윤인섭 ( In Sub Yun ),최우혁 ( Woo Hyuk Choi ),허병기 ( Byung Ki Hur ),강동국 ( Dong Gug Kang ) 한국고무학회 2010 엘라스토머 및 콤포지트 Vol.45 No.3
리튬 이온 전지의 가스켓 재료로 사용되기 위해서는 내전해액성, 전기절연성, 낮은 압축 영구 줄음률, 비오염성, 내열성이 요구된다. Perfluoroalkoxy (PFA)보다 압축 영구 줄음률이 우수한 고무의 적합성을 평가하기 위하여 Ethylene Propylene Diene Monomer (EPDM), Nitrile Butadiene(NBR), Fluoro Elastomers(FKM), Methyl-Vinyl Silicone Rubber (VMQ), Fluorosilicone(FVMQ)을 이용하여 최적상태의 compound를 제작하고 특성을 살펴보았다. 시험편을 80 ℃의 propylene carbonate액에 침적하여 경도 및 체적변화를 1,000시간까지 시간별로 측정하였다. EPDM과 VMQ가 내전해액성이 우수하였으며, 전기절연성에서도 체적저항 기준 10(10)Ωcm이상의 결과를 얻을 수 있었다. 따라서, EPDM과 VMQ가 적절한 것으로 판단되었다. The materials of the lithium ion battery gasket require chemical resistance to the electrolyte, electrical insulating, compression set, anti-contamination and heat resistance. To estimate suitability for rubber which has better performance to compression set than PFA, each compound were made with various rubbers, such as EPDM, NBR, FKM, FVMQ, VMQ and we checked the characteristics of each compound. Samples from each compound was deposited in Propylene Carbonate and tested for changing of Hardness and Volume during 1,000 hr with 80 ℃. EPDM and VMQ showed good performance to chemical resistance to the electrolyte, and also we could get the values over 10(10)Ωcm on volume resistance basis in electrical insulating. EPDM and VMQ were judged as the most suitable material.