김혜성,이종필,박동규,안인섭,Kim, Hye Seong,Lee, Jong Pil,Park, Dong Kyu,Ahn, In Shup 한국분말야금학회 2013 한국분말재료학회지 (KPMI) Vol.20 No.6

In this study, analysis on the oxidation behavior was conducted by a series of high-temperature oxidation tests at both $800^{\circ}C$, $900^{\circ}C$ and 1000 in the air with sintered STS 316L. The weight gain of each oxidized specimen was measured, the oxidized surface morphologies and composition of oxidation layer were analyzed with Scanning Electron Microscope-Energy Dispersive x-ray Spectroscopy (SEM-EDS), finally, the phase change and composition of the oxidized specimen were shown by X-Ray Diffraction (XRD). As a result, the weight gain increased sharply at $1000^{\circ}C$ when oxidation test was conducted for 210 hours. Also, a plentiful of pores were observed in the surface oxidation layers at $900^{\circ}C$ for 210 hours. In addition, the following conclusions on oxidation behavior of sintered STS 316L can be obtained: $Cr_2O_3$ can be formed on pores by influxing oxygen through open-pores, $(Fe_{0.6}Cr_{0.4})_2O_3$ can be generated on the inner oxidation layer, and $Fe_2O_3$ was on the outer oxidation layer. Also, $NiFe_2O_4$ could be precipitated if the oxidation time was kept longer.

Effect of Composition of Bond Coating on the Durability of the Plasma Sprayed $\textrm{ZrO}_2$-$\textrm{CeO}_2$-$\textrm{Y}_2\textrm{O}_3$ Thermal Barrier Coating

김혜성,김병희,서동수,Kim, Hye-Seong,Kim, Byeong-Hui,Seo, Dong-Su Materials Research Society of Korea 1999 한국재료학회지 Vol.9 No.1

The effect of alloy compositions of the bond coating on the plasma sprayed-thermal barrier coatings was investigated. The performance of the coating composed of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ and Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$was evaluated by isothermal and thermal cyclic test in an ambient atmosphere at 115$0^{\circ}C$. The failure of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coatings was occurred at the bond coating/ceramic coating interface while Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$ coating was failed at the substrate/bond coating interface after thermal cyclic test. The lifetime of Rene80/NiCrAl/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coatings was longer than Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$coating. The oxidation rate of the NiCrAl bond coating examined by TGA was lower than CoNiCrAlY bond coatings. In summary, these results suggest that Rene80/CoNiCrAlY/ZrO$_2$-CeO$_2$-Y$_2$O$_3$system as thermal barrier coating be not suitable considering the durability of the coating layer for high temperature oxidation and thermal stress.

급냉응고법에 의한 In-Situ 복합재료로서의 과포정 Al-10wt%Ti 합금(I)

김혜성,금동화,김긍호,Kim, Hye-Seong,Geum, Dong-Hwa,Kim, Geung-Ho 한국재료학회 1999 한국재료학회지 Vol.9 No.3

In this study, a new concept of aluminum-matrix composites and the possibility of in-situ processing are suggested, and preliminary results on AI- Ti system are presented. Fine powders of AI-lO% Ti were prepared by the gas atomization so that fine $Al_3Ti$ formed into flake shape. A 25v/o $Al_3Ti/Al$ composite sample was made by the pow­d er metallurgy process involving hot extrusion. Microstructure and mechanical behavior both at room temperature and high temperatures were analysed by OM, SEM, TEM and tension test. Microstructural characteristics and mechanical properties of the composites exhibited similar behavior to those of $SiC_w/2124$ composites. Merits and drawbacks of the $Al_3Ti/Al$ composites are discussed together with a possibility of further improvement. 본 연구에서는 Al-기지 복합재료의 새로운 개념과 in-situ 공정의 가능성을 Al-Ti계의 연구결과들을 토대로 제시하고자 하였다. 가스아토마이제이션법에의해 $Al_3Ti$가 미세한 편상형상을 갖도록 Al-10%Ti 조성의 합금분말을 제조하고, 고온 압출 공정을통하여 25V/o $Al_3Ti/Al $ 복합재를 제조하였다. 복합재의 미세구조를 광학현미경, SEM, TEM 등을 이용하여 조사하였고, 상온과 고온에서의 기계적 특성을 인장시험을 통하여 측정하였다. 제조된 복합재료의 미세구조 및 고온 기계적 성질을 상용되고 있는 $SiC_w/2124$ 복합재료와 유사한 거동을 보여준다. 제조된 $Al_3Ti/Al$ 복합재료의 장점과 단점이 물성향상의 가능성과 더불어 제시되었다.

STS 316L 소결재료의 내식특성에 미치는 합금원소 첨가방법의 영향

김혜성,김유영,박동규,안인섭,Kim, Hye Seong,Kim, Yoo Young,Park, Dong Kyu,Ahn, In Shup 한국분말야금학회 2013 한국분말재료학회지 (KPMI) Vol.20 No.3

In this study, STS 316L powders with 3 wt.% Cu and 1 wt.% Sn known as corrosion-resistance reinforcement elements, are prepared to make different kinds of specimens, in which, 3 wt.% Cu and 1 wt.% Sn are added in different forms by mixing, alloying and fully alloying. After sintering in the same condition, the corrosion resistance, wear resistance and their mechanical properties of specimens are tested respectively. According to the comparison, STS 316L specimen sintered at $1270^{\circ}C$ showed the most excellent mechanical property: HRB 78 (hardness), 1130.7 MPa (RCS), 26.6% (Fraction Wear), It was similar with the specimen made of STS316L and fully alloyed Cu and Sn powders, meanwhile, the latter one appears the best corrosion resistance, 75hrs-salt immersion test results. In addition, the specimens with Cu and Sn powders additive showed relatively worse wear resistance in compared with STS316L specimen.

급냉응고법에 의한 In-Situ 복합재료로서의 Al-10wt%Ti-4wt%Fe 합금 (II)

김혜성,정재필,권숙인,금동화,Kim, Hye-Seong,Jeong, Jae-Pil,Gwon, Suk-In,Geum, Dong-Hwa 한국재료학회 1998 한국재료학회지 Vol.8 No.12

본 연구에서는 Al-10wt%Ti-4wt%Fe 복합재료를 in-situ공정으로 제조할 수 있는 가능성 및 2 원계 Al-10wt%Ti 복합재료의 낮은 기계적 성질(탄성계수, 상온 고온강도, 내마모특성 등)을 PM SiC/2124 복합재료 수준 흑은 그 이상으로 향상시킬 수 있는 가능성을 조사하였다. 제조된 Al-10wt%Ti-4wt%Fe 합금은 불연속 SiC 강화상으로 보강된 Al-기지 복합재료($SiC{w}$/2124)와 유사한 미세구조를 보여주었으며, 탄성계수 및 인장강도, 내마모성질 등의 기계적 특성이 2원계 Al-10%Ti 합금각 비교해 현저하게 향상되었음이 관찰되었다. 위의 결과는 초정 $Al_3Ti$상 외에도 Fe 원소의 첨가를 통한 추가적인 $Al_{x}Fe$의 분산강화 효과에 기인한 것으로 해석된다. The possibilities of producing Al-10%Ti-4%Fe composites through in-situ processing and thus achieving mechanical property improvements over binary Al-10%Ti to a level or higher exhibited by PM SiC/A12124 composites were explored in this study. The microstructure of in-situ processed Al-10%Ti-4%Fe composites was similar to that of Al matrix composites reinforced with discontinuous SiC particulates(SiC/A12124) and significant enhancements in elastic modulus, tensile strength and wear resistance were observed as compared to Al-10%Ti alloy. These results can be attributed to the in-situ formed Al. Fe by third element addition, leading to additional dispersion strengthening effect over $Al_3Ti$ phase reinforcement in Al-Ti system.

포커스 - 해외연수 결과보고: 제23차 방재공직자 호주.뉴질랜드 해외연수

김혜성,Kim, Hye-Seong 한국방재협회 2012 방재저널 Vol.14 No.1

사례분석에 의한 강구조 스타디움 레일 시스템 분류

김혜성,윤성원,Kim, Hye-Seong,Yoon, Sung-Won 한국공간구조학회 2010 한국공간구조학회지 Vol.10 No.1

국내에 설치될 강구조 스타디움에 향후 신재생에너지 중 하나인 태양광 발전을 위한 PV 시스템을 적용하는 것에 따른 강재 어레이에 관한 기초 연구로 해외의 사례를 토대로 구성되었다. 연구를 진행하기 위하여 1990년대 이후 PV 시스템이 적용된 강구조 스타디움 20건을 사례 분석 대상으로 선정하였다. 선정된 20건의 강구조 스타디움을 PV 모듈을 고정하기 위하여 설치된 레일 시스템에 따라 분류해 보았다. 그 결과 격자고정방식 중 선형모듈고정방식과 지붕 통합형이 전체의 28%에 해당되는 것으로 조사되었으며 그 뒤로 레일 고정형 17%, 세로 고정방식 중 모듈그룹 고정 11% 순으로 조사되었다. 또한 스타디움 내부에는 주로 격자 고정방식 중 선형모듈 고정방식과 지붕통합형이 적용되고 있었으며 스타디움 외부나 그 외 부분에서는 앵글 브라킷으로 PV 모듈이 고정되고 있는 것으로 조사되었다. This paper focuses on steel arrays regarding the application of PV system for solar power system, a renewable energy in steel structure stadium that will be built in Korea, by foreign case study. 20 cases of Steel Structure Stadiums applying PV system after 1990 were selected as the main subjects. The 20 cases of Steel Structure Stadiums were categorized by rail systems that were installed to fix PV module. As the result, linear clamping and roof-integrated type among cross rails were 28% of the whole, followed by 17% of rail-fixed type and 11% of module group-fixed type among vertical-fixed types. In addition, linear clamping and roof-integrated type among cross rails were applied in the inside of the stadium while the outside and other parts of stadiums used angle bracket to fix PV module.

베르크손에서 지성과 직관 -이분법을 넘어서-

김혜성 ( Kim Hye-seong ) 경희대학교 인문학연구원 2019 인문학연구 Vol.0 No.40

일반적으로 베르크손에서 지성과 직관의 차이는 실용적 관점과 순수 관조의 차이로 이해된다. 이런 이분법의 관점에서는 그 두 인식의 차이는 뚜렷하게 비교되나 그것들의 상호 관계는 해명되기 어렵다. 이는 지성과 직관에 대한 충분한 이해가 되지 못할 뿐만 아니라, 베르크손에서 철학과 과학, 삶과 철학 사이의 갈등을 극단화하는 해석의 문제를 일으킬 수 있다. 지성은 실용적이기에 철학적 진리에서 배제되고 직관은 유용함과 거리가 멀기에 삶과 무관한 것처럼 보이게 되는 것이다. 따라서 지성과 직관의 관계에 대한 베르크손의 생각에 주목함으로써 이분법을 보완해야 한다. 그에 따르면, 과학은 물질에 대한 형이상학적 인식으로 인정되며, 직관은 단지 보는 것이 아닌 작용하는 것으로서 삶에 기여한다, 결국 직관의 철학은 지성의 거부와는 무관한 것으로, 지성주의라는 습관에서 벗어나 지성을 사용하는 새로운 습관 형성의 문제이다. 이렇게 보면, 이분법적 관점에서 강조되는 개념에 대한 이미지의 우선성을 다르게 볼 여지도 있다. 이미지보다 지성의 개념이 중요하며, 직관의 철학은 다수의 지성들이 서로 겹쳐지는 지적 협력의 지속으로 이해 될 수 있다. Generally, the intelligence and the intuition in Bergson tend to be interpreted with a dichotomous framework; the former is a practical perspective, while the latter is a pure contemplation. This approach, despite its advantages to explain their opposition, can make obscure their rapport. But if the intuition is without any connection with rationality, the science should be excluded from the philosophical thought, and the philosophy of intuition can be reduced to a mere irrationalism. Besides, in this condition, it becomes difficult to recognize the benefit of philosophy, since the intuition is simply characterized by a disinterested knowledge in its opposition to practical intelligence. Therefore, as a complementary perspective, it is necessary to examine the relationship between intuition and intelligence. In fact, Bergson's philosophy assigns a metaphysical status to the science, and his concept of intuition is not simply a pure speculation but also an acting thing; the intelligence actually engages in philosophical thinking, and the intuition has an impact on our daily lives. Thus, Bergson’s philosophy of intuition has nothing to do with a refusal of intellectuality; its goal is just to get a new habit of using the intelligence without intellectualism. From this approach, the possibility of rethinking the priority of image over concept is open to us; concept is more important than image, and the philosophy of intuition can be understood as a progressive intellectual cooperation, that is, a continuous process of superposition of multiple intelligences.

태양광을 이용한 강구조 공공시설물의 public art

김혜성(Hye Seong Kim),이경희(Kyoung Hee Lee),윤성원(Sung Won Yoon) 한국강구조학회 2008 韓國鋼構造學會誌 Vol.20 No.2

수산부문 기술분야별 특허의 경제적 기대효과 분석 -국립수산과학원 기술개발 사례를 중심으로-

김혜성(Hye-Seong KIM),민병화(Byung Hwa MIN),이정용(Jeong Yong LEE),김현철(Hyun Chul KIM),이주현(Ju-Hyun YI),김도훈(Do-Hoon KIM) 한국수산해양교육학회 2021 水産海洋敎育硏究 Vol.33 No.4