김대건,김은표,김영도,Kim, Dae-Geon,Kim, Eun-Pyo,Kim, Yeong-Do 한국재료학회 2002 한국재료학회지 Vol.12 No.1
In this study, the 95W heavy alloys of 3/7, 5/5 and 7/3 of Ni/Fe ratio were sintered at the temperature range between 1420 and $1480^{\circ}C$ for 1h and their microstructures were discussed for an effect of the ${\mu}$-phase $(Fe_7W_6)$ on the microstructure. The ${\mu}$-phase was observed in the only 95W-1.5Ni-3.5Fe alloy of 3/7 and it is thought to be formed and grown from the surface of the W particle. The W particle was surrounded with the ${\mu}$-phase and there were only the W particles and this phase without Ni-Fe-W matrix at the most part. The ${\mu}$-phase changed the interphase structure in the alloy and the grain growth of the W was suppressed because of interrupting the solution-reprecipitation of the W. The W content in the matrix was considered to be lowered due to the interruption of the solution-reprecipitation and the formation of the ${\mu}$-phase in the .
24개월 대기 노출된 Al1050 및 Al7075 알루미늄 합금 산화막에 대한 투과전자현미경 분석
김대건,김가림,최원준,반치범,Kim, Dae-Geon,Kim, Ga-Rim,Choi, Wonjun,Bahn, Chi Bum 한국표면공학회 2019 한국표면공학회지 Vol.52 No.2
Al1050 and Al7075 alloy specimens were exposed to atmospheric conditions for 24 months and analyzed by Transmission Electron Microscopy to characterize their corrosion behavior and oxide film characteristics, especially focusing on intergranular corrosion or oxidation. In general, the intergranular oxygen penetration depth of Al1050 was deeper than Al7075. Since O and Si signals were overlapped at the oxidized grain boundaries of Al1050 and Mg is not included in Al1050, it is concluded that Si segregated along the grain boundaries directly impacts on the intergranular corrosion of Al1050. Cr-Si or Mg-Si intermetallic particles were not observed along the grain boundaries of Al7050, but Mg-Si particle was barely observed in the matrix. 10-nm size Mg-Zn particles were also found all over the matrix. Mg was mainly observed along the oxidized grain boundary of Al7075, but Si was not detected due to the Mg-Si particle formation in the matrix and relatively low concentration of Si in Al7075. Therefore, it is thought that Mg plays an important role in the intergranular corrosion of Al7075 under atmospheric corrosion conditions.
김대건,Kim, Dae-Geon 한국통신학회 2007 정보와 통신 Vol.24 No.4
컨버전스시대의 꽃이라고 할 수 있는 IPTV 서비스는 세계 유수의 통신 사업자들을 중심으로 현재 빠르게 추진되고 있다. 이러한 IPTV 서비스의 세계적 추세에서 우리나라는 자타가 공인하는 세계 제일의 브로드밴드 강대국으로서, 이는 향후 다가올 컨버전스 시대에 강한 경쟁력 우위를 점할 수 있는 더할 수 없는 기회이다. 이에 본 기고에서는 IPTV에 관한 개요, 정책, 서비스, 요소기술, 국내외 현황 및 표준화에 대해 기술한다.
황칠나무 추출물을 12주간 음용한 비알코올성지방간(NAFLD) 비만대학생들에게 미치는 영향
김대건(Dae-Geon Kim),황길수(Gill-Su Huang) 한국엔터테인먼트산업학회 2012 한국엔터테인먼트산업학회 학술대회 논문집 Vol.2012 No.11
본 연구는 황칠나무 추출물이 비알코올성지방간(NAFLD)을 가진 비만대학생들에게 음용하게 한 후 aspartate aminotransferase(AST)와 alanine aminotransferase(ALT)를 측정하여 효능을 검증해 보고자 하였다. 부산지역 대학생 중 전문의에 의한 의학적 검진을 실시한 후 체지방율이 25%이상인 20대 비알코올성 지방간을 가진 비만 남자대학생을 대상으로 음용군 10명, 대조군 10을 선정하여 12주 동안 1일 2회 조식과 석식 전 공복에 1회 용량 60ml를 음용하게 하였다.SPSS 17.0 Windows 소프트웨어를 이용하여 모든 변인의 측정결과를 평균과 표준편차를 산출하고, 음용전과 12주 후의 차이검증과 그룹간의 차이검증은 이원분산분석(Two-way ANOVA)을 이용하여 통계적 유의수준은 p<.05로 하였다. 결과는 황칠나무 추출물은 비알코올성지방간(NAFLD)을 가진 비만대학생들에게 AST와 ALT에 효과가 있는 것으로 나타났다. 그리고 BMI에서도 효과는 나타냈지만, 이는 어떠한 원인 때문에 효과가 나타났는지는 후속 연구가 필요하다고 사료된다.
습윤양생 장치를 이용한 아파트 측벽 균열제어에 관한 연구
김대건 ( Kim Dae-geon ),이동운 ( Lee Dong-woon ) 한국건축시공학회 2017 한국건축시공학회지 Vol.17 No.2
최근 국내 아파트의 외벽 거푸집공사의 경우 대부분 갱폼시스템을 통해 철근콘크리트 구조체를 시공하고 있다. 이러한 갱폼거푸집을 사용한 콘크리트의 경우는 거푸집 탈형후 외부환경에 노출되고 특히, 건조한 봄, 가을과 일사량이 높은 서중시기의 벽량이 많은 아파트 측벽에 다량의 균열이 발생되어지고 있다. 이에, 본 연구에서는 신축 아파트 건설현장 중심으로 균열량이 많은 아파트 측벽부분의 갱폼시스템에 습윤양생 자동설비장치를 적용하여 초기 콘크리트 양생에 필요한 수분을 공급함으로써 콘크리트의 품질확보와 다량의 측벽균열 저감을 통한 습윤양생 자동장치의 효율성 및 활용성을 검토하고자 하였는데, 그 결과, 양생 효과 및 낙수량 고려 시 습윤양생 자동장치에 0.3mm 사이즈의 노즐을 사용하여 살수양생을 실시할 경우, 자원낭비 없이 콘크리트의 품질향상 및 균열저감에 효과적인 것으로 판단되었다. In this study, moist curing equipment was used in the exist gang-form system. By achieving sufficient spray curing, the quality of the concrete was improved and the cracking occurred in building`s side wall was decreased. The following results could be made as the conclusion. For the compressive strength, all zones showed the similar results. Comparing with the zone without using moist curing equipment, the zone used moist curing equipment showed higher rebound hardness results. For the cracking, the zone utilized moist curing equipment showed the cracking averaged as 6.6m and the zone without using moist curing equipment showed the cracking averaged as 10.3m. The effectof reducing cracking by utilizing moist curing equipment is about 36%. Using moist curing equipment is considered as a good solution to reduce the cracking in the structure. Considering all the factors analysed, using moist curing equipment improved the quality of the concrete and decreased the cracking. When this equipment was used in the construction site, it is expected that the construction periodcan be shrunk and the ratio of defect caused by drying shrinkage can be decreased. In this research conditions, The 0.3mm sized moist curing equipment provided the most desirable results on concrete quality and preventing cracking.
바탕콘크리트의 라텍스 혼입에 따른 복합열화 저감에 관한 연구
김대건 ( Kim Dae-geon ) 한국건축시공학회 2023 한국건축시공학회 학술발표대회 논문집 Vol.23 No.1
This study aims to mix the base concrete by mixing latex to improve the durability performance to reduce the composite deterioration of the base concrete. Latex fiber has high resistance to freezing and thawing, adhesion, and deicing agent (calcium chloride), and it is used to secure long-term durability to reduce cracking and compound deterioration of concrete. In addition, through experiments, we are trying to find ways to improve the strength of concrete by studying the mixing of the appropriate mixing ratio of latex.
화재안전을 위한 BIM기술과 드론 및 IT융복합 기술을 접목시킨 소방안전시스템 구축
김대건 ( Kim Dae-geon ),이기휘 ( Lee Gi-hwi ),홍일혁 ( Hong Il-hyeok ),김민성 ( Kim Min-sung ),이동운 ( Lee Dong-oun ) 한국건축시공학회 2018 한국건축시공학회 학술발표대회 논문집 Vol.18 No.1
While damage caused by fire increases, awareness of fire is still low. Morever, Small fires often spread into big fires as they fail to keep the golden time due to the delay in initial response. In particular, the initial response is more important in areas where many unauthorized buildings are called "Panjachon" as firefighting facilities are insufficient compared to other residential facilities. Therefore, we will combine BIM technology, drones and IT convergence technologies to develop a firefighting safety information system that can speed up initial response and help combat fires.
외벽 콘크리트 균열하자 계측을 위한 고층 구조물 외벽 유지관리용 지능형 로봇시스템 개발
김대건(Kim, Dae Geon),김복규(Kim, Bok Kyu) 한국구조물진단유지관리학회 2011 한국구조물진단학회 학술발표회논문집 Vol.15 No.1
This study aims to measure a crack property quantitatively through a unmanned automatic robot system for a concrete wall of high-rise buildings apt to age by being exposed to an open air environment. Through this, we aim to present the application of efficient repairs and reinforcement by deterioration phenomena by deriving a plan to measure cracks in reinforced concrete accounting for most of the lawsuits against defects in the current apartment houses with scientific and objective data.