플라즈마 코팅한 주조용 알루미늄합금의 마찰 및 마멸특성
채영훈,임정일,박준목,김석삼,Chae, Young-Hun,Ren, Jing-Ri,Park, Jun-Mock,Kim, Seock-Sam 대한기계학회 1997 大韓機械學會論文集A Vol.21 No.5
The wear characteristics and wear mechanisms of plasma sprayed Al/sub 2/ O/sub 3/-40%TiO/sub 2/ and Cr/sub 2/O/sub 3/ deposited on casting aluminum alloy(AC4C) were investigated. Specimens were processed for various coating thicknesses. Ball on disk type wear tester was used for wear test. The scratch test on plasma sprayed coating surface showed that critical load to break the coating layer was greater than 40 N. The critical load increase with the increase of coating thickness of specimens. The friction coefficient of Cr/sub 2/O/sub 3/ coating layer was less than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. The wear resistance of Cr/sub 2/O/sub 3/ coating layer was greater than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. Microscopic observation of worn surfaces was made by SEM. SEM observation showed that the main mechanism of wear for Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer was abrasive wear under 50 N. For the case of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer, as the surface cracks perpendicular to sliding direction propagated, the wear debris was generated in wear track. However, the main mechanism of wear for Cr/sub 2/O/sub 3/ coating layer was brittle fracture under 150 N.
채영훈,박병희,김석삼,Chae, Young-Hun,Park, Byung-Hee,Kim, Seock-Sam 대한기계학회 1999 大韓機械學會論文集A Vol.23 No.7
The sliding wear behavior of $Al_2O_3/NiCr$ coating deposited on steel(SM45C) was investigated under lubrication. The parameters of sliding wear are normal loads, coating thickness. As a result, the wear resistance of $Al_2O_3/NiCr$ coating was remarkably greater than that of $Al_2O_3$ coating. The optimized coating thickness was found to be $300{\mu}m$ to ensure good anti-wear. The bond coating played important role in decreasing residual stress. The residual stress had much influence on wear mechanism. These results were correlated with the stress state of coating and the microstructure of coating.