( Sarah Augustina ),( Imam Wahyudi ),( I Wayan Darmawan ),( Jamaludin Malik ),( Efrida Basri ),( Yoichi Kojima ) 한국목재공학회 2020 목재공학 Vol.48 No.4
Effect of pre-treatment and compression ratio on specific gravity (SG) and dimensional stability improvement of three lesser-used wood species from natural forest area of North Kalimantan Province, Indonesia had been investigated. Hot soaking at 80 ℃ for 3 hours within 2 and 5% of boron solution was applied as pre-treatment, while compression ratio applied was 20 and 40% from the initial thickness. Densification was conducted using hot pressing machine at 30 kg/cm<sup>2</sup> of pressure and 160 ℃ of temperature for 15 minutes. Specific gravity was measured gravimetrically, while dimensional stability was evaluated through thickness swelling and water absorption as the indicator. Results show that SG of densified wood was influenced by wood species and compression ratio, but not by pre-treatment applied; while dimensional stability was influenced by wood species, compression ratio, and pre-treatment. Specific gravity and water absorption of densified wood was improved significantly. Specific gravity increased 28.86-63.03%, while water absorption decreased 12.80-15.89%. Thickness swelling of 20% densified wood was lower than that of 40% densified wood.
( Sarah Augustina ),( Sari Delviana Marbun ),( Sudarmanto ),( Narto ),( Deazy Rachmi Trisatya ),( Eko Budi Santoso ),( Dhimas Pramadani ),( Nanda Nur Afni ),( Tushliha Ayyuni Fariha ),( Gabriel Wiwind 한국목재공학회 2023 목재공학 Vol.51 No.6
Samama wood (Anthocephalus macrophyllus (Roxb) Havil) is a fast-growing and lesser-utilized wood species that has inferior properties; therefore, its quality needs to be improved. This research aimed to determine the effect of citric acid impregnation at high curing temperatures on the dimensional stability and mechanical properties of wood. Citric acid solution with 10% concentration (w/w) was impregnated into wood samples by vacuum-pressure method (-0.5 cmHg, 30 min; 0.7 MPa, 3 h), followed by curing process at 140℃, 160℃, and 180℃ of temperature for 1 h. In comparison, the other wood samples were heat treated at the same temperatures and time. The results showed that the increase in curing and heat temperatures for both treatments were directly proportional to the dimensional stability, but inversely proportional to the mechanical properties. Citric acid impregnated had higher density, dimensional stability, and mechanical properties, except for modulus of rupture, than that of heat treatment. The optimum temperature is suggested at 160℃ in both treatments.