( Efrida Basri ),( Saefudin ),( Mahdi Mubarok ),( Wayan Darmawan ),( Jamal Balfas ),( Yelin Adalina ),( Yusuf Sudo Hadi ) 한국목재공학회 2023 목재공학 Vol.51 No.6
This study is a continuation of our previous work, which focused on the resistance of jabon wood to termites after impregnation with wood vinegar (WV) and animal-based adhesive (kak). This paper presents the physicomechanical properties of fast-growing jabon wood impregnated with kak at two concentrations (8% and 10%) in wood vinegar or water as a solvent with and without 4% borax. The physical properties of the impregnation solution, that is, viscosity, density, pH, and solid content, were evaluated according to SNI 06-4567-1998. Some physical parameters, such as weight percent gain (WPG), density, water uptake, anti-swelling efficiency (ASE), crystallinity, and mechanical properties, i.e., modulus of elasticity (MOE), modulus of rupture (MOR), and compression strength parallel to the grain (CS), of the impregnated wood were determined. Based on these results, wood impregnated using a mixture of kak in WV presented better physical (increased WPG, density, dimensional stability, and crystallinity) and mechanical (increased MOE/MOR and compression strength) properties than wood impregnated with a water solvent or untreated wood. The wood impregnated using WV and water solvent improved the physical and mechanical properties. The density of the wood increased by 44%-58% and 32%-47%, ASE radial-tangential increased by 38%-45%; 15%-28% after 24 h of water immersion, crystallinity increased by 59%-74%; 36%, MOE increased by 46%- 57%; 28%-31%, MOR increased by 29%-34%; 14%-27%, and compression strength increased by 40%-76%; 38%-72% values to untreated wood.
-
( Wa Ode Muliastuty Arsyad ),( Efrida Basri ),( Djeni Hendra ),( Deazy Rachmi Trisatya ) 한국목재공학회 2019 목재공학 Vol.47 No.4
Jabon (Anthocephalus cadamba Miq.) is a fast-growing species that exhibits a lower natural resistance than that exhibited by the timber sourced from natural forests. Jabon’s resistance to termite attack can be improved by impregnating its wood structure with poisonous organic materials. This study examined jabon’s resistance to termite attack when impregnated with wood vinegar and an animal adhesive. The wood specimens were impregnated using sengon wood vinegar and an animal adhesive (8% and 10%, respectively) using a vacuum pressure machine. The specimens were tested for their resistance to subterranean and dry-wood termites according to Indonesian National Standard (SNI 7207-2014). The results denoted that jabon impregnated with wood vinegar and an animal adhesive concentration of at least 8% with the addition of 4% borate was effective to resist termite attacks. The impregnated jabon exhibited a lower weight loss and higher termite mortality when compared with those exhibited by the control specimens. Thus, the resistance class improved from class IV to class I.
-
( Sarah Augustina ),( Imam Wahyudi ),( I Wayan Darmawan ),( Jamaludin Malik ),( Efrida Basri ),( Yoichi Kojima ) 한국목재공학회 2020 목재공학 Vol.48 No.4
Effect of pre-treatment and compression ratio on specific gravity (SG) and dimensional stability improvement of three lesser-used wood species from natural forest area of North Kalimantan Province, Indonesia had been investigated. Hot soaking at 80 ℃ for 3 hours within 2 and 5% of boron solution was applied as pre-treatment, while compression ratio applied was 20 and 40% from the initial thickness. Densification was conducted using hot pressing machine at 30 kg/cm<sup>2</sup> of pressure and 160 ℃ of temperature for 15 minutes. Specific gravity was measured gravimetrically, while dimensional stability was evaluated through thickness swelling and water absorption as the indicator. Results show that SG of densified wood was influenced by wood species and compression ratio, but not by pre-treatment applied; while dimensional stability was influenced by wood species, compression ratio, and pre-treatment. Specific gravity and water absorption of densified wood was improved significantly. Specific gravity increased 28.86-63.03%, while water absorption decreased 12.80-15.89%. Thickness swelling of 20% densified wood was lower than that of 40% densified wood.