용접조건 변수가 복합 구조물 용접부의 변형과 수축 특성에 미치는 영향 연구 = A Study on the Effects of Welding Process Variables on the Distortion and Shrinkage Characteristics of Welded Joints in Complex Structures

다국어 초록 (Multilingual Abstract)

After tack welding the composite container material（SS-400, 10t） in the form of V-type groove butt, T-type fillet, and corner according to the drawing, the dimensions were measured and welded. As a result of analyzing the deformation of the composite container after welding, the occurrence of deformation was large in the order of angle welding 〉 T-type fillet welding 〉 butt welding. By posture, the deformation of the horizontal posture was greater than that of the vertical posture.
As a result of checking the defects by conducting a radiation transmission test, there were many defects in the order of fillet welding〉 angle welding 〉 butt weld. Among the defects, the pores were the most defective, and it was found that the slag inclusion occurred a lot. It was found that relatively few cracks occurred.

국문 초록 (Abstract)

도면에 따라 복합 용기 재질（SS-400, 10t）을 V형 맞대기 용접（V-groove butt joint）, T형 필렛 용접（T-type fillet joint）, 그리고 모서리 용접（corner joint）으로 가접한 후 치수를 확인하고 본용접을 수행하였다. 용접 후 복합 용기의 변형을 분석한 결과, 변형량은 모서리 용접 〉 T형 필렛 용접 〉 맞대기 용접 순으로 크게 발생하였다. 또한 용접 자세에 따른 변형은 수평 자세에서 수직 자세보다 더 크게 발생하는 경향을 보였다.
방사선 투과시험（RT）을 통해 용접부의 결함을 평가한 결과, 결함 발생 빈도는 필렛 용접, 모서리 용접, 맞대기 용접의 순으로 높게 나타났다. 결함 종류별로는 기공이 가장 높은 발생 빈도를 보였으며, 슬래그 혼입 또한 다수 관찰되었다. 반면, 균열의 발생은 상대적으로 적은 것으로 확인되었다.

목차 (Table of Contents)

• Ⅰ. 서론 1
• 1. 연구 배경 1
• 2. 연구 목표 26
• Ⅱ. 시편의 준비 및 실험방법 27
• 1. 시편의 준비 27
• 2. 용접 실험 조건 30
• 3. 실험방법 31
• Ⅲ. 실험 및 고찰 33
• 1. 복합용기 가접부와 용접부의 치수 변화 및 변형도 비교· 33
• 2. 방사선투과시험 검토 46
• Ⅴ. 결론 50
• 참고문헌 52
• 영문초록 55